论文部分内容阅读
【摘要】前几年的住宅建设中，钢筋混凝土预制板是构成砖混结构房屋的重要构件，其本身由于在构造上存在着一些致命的缺陷，即整体性及抗震性差，因此，在近几年的住宅建设中它逐步被钢筋混凝土现浇板所替代。随着钢筋混凝土现浇板在房屋建设中的大量推广与应用，“住宅楼现浇楼板裂缝问题”也成了居民住宅质量投诉热点。本文主要从施工方面､兼顾设计和材料原因方面分析楼面裂缝的综合防治措施。
【关键词】楼面；裂缝；分析
By floor concrete present pour liquid on board quality question and preventing and controlling measure
Zhang Xuemei
【Abstract】A few years ago the housing construction， prefabricated reinforced concrete masonry structure constitutes an important component housing， Since its construction in the presence of some fatal flaw， that is integrated seismic and poor， Therefore， in recent years it gradually residential buildings are cast-in-place reinforced concrete plate has been replaced. Along with cast-in-place reinforced concrete plate at the building housing the massive promotion and application “Residential building of cast-in-place slab cracks” became residential quality to bring complaints hot. This paper mainly from the construction， design and material balance reason for the analysis of the floor cracks comprehensive prevention and control measures.
【Key words】Floor；Crack；Analysis
【中圖分类号】TU50【文献标识码】B【文章编号】1005-250X(2008)01-0044-03
1 钢筋混凝土现浇板裂缝原因的分析
一般情况下，楼面裂缝表现为：表面龟裂，纵向､横向裂缝以及斜向裂缝。主要有设计､混凝土原材料及施工等三方面的原因。
1.1 设计方面
1.1.1 地基的不均匀沉降：在住宅建设中，有相当一部分的钢筋混凝土现浇板的裂缝，是由于地基不均匀沉降的原因而造成的。如在软土地基下采用扩展基础，则对于那些相对较长的条式楼来说，要想保正它们沉降均匀是相当困难的，因此，有时也会由于基础的不均匀沉降，而引起楼房的拉裂和钢筋混凝土现浇板的开裂。
1.1.2 荷载的作用：在住宅建设中，也有少部分钢筋混凝土现浇板的裂缝，是由于荷载作用方面的原因引起的。由于设计人员在进行现浇板的配筋计算过程中，通常只是根据其承载能力来确定配筋量的，而往往忽略了对板在正常使用阶段，其承受的荷载而引起的挠度及裂缝宽度的验算，故而引起裂缝的产生，这些裂缝有时也会超过规范的最大允许值，这也应当引起足够的重视。
1.1.3 结构体型突变及未设置必要的伸缩缝：房屋长度过长，而又未考虑设置伸缩缝，当房屋的自由伸缩达到应设置伸缩缝要求的间距时，就要引起裂缝的产生。另外，平面布局凹凸较多，即转角越多，一受到混凝土收缩及温差变化易于产生裂缝。
1.1.4 在楼房的设计中，设备专业特别是电气专业，大多将照明､有线电视､通讯等所需的管线直接敷设于现浇板中，而且有时集中于某一处现浇板中的管线多达7-8根，并且这些管线的直径多为2-3cm，由此就会使该处的现浇板厚度大大削弱，从而引起现浇板在该处开裂。
1.2 混凝土原材料质量方面
1.2.1 水泥凝结或膨胀不正常，如水泥安定性不稳定，水泥中含有生石灰或氧化镁，这些成分在和水化合后产生体积膨胀，产生裂缝。
1.2.2 如果骨料中含泥量过多，则随着混凝土的干燥，会产生不规则的网状裂缝。
1.2.3 碱——骨料反应：蛋白质､安山岩､玄武岩､辉绿岩等碱性骨料有可能与碱性很强的水泥起化学反应，生成有膨胀能力的碱——硅凝胶而引起混凝土膨胀破坏，产生裂缝。
1.2.4 水灰比､塌落度过大或使用过量粉砂混凝上强度值对水灰比的变化十分敏感，基本上是水和水泥计量变动对强度影响的叠加。因此，水､水泥､外渗混合材料外加剂溶液的计量偏差，将直接影响混凝土的强度。如采用含泥量大的粉砂配制的混凝土收缩大，抗拉强度低，容易因塑性收缩而产生裂缝。
1.3 施工质量方面
1.3.1 混凝土施工过分振捣，模板､垫层过于干燥。混凝土浇筑振捣后，粗骨料沉落挤出水分､空气，表面呈现泌水而形成竖向体积缩小沉落，造成表面砂浆层，它比下层混凝土有较大的干缩性能，待水分蒸发后，易形成凝缩裂缝。而模板､垫层在浇筑混凝上之间洒水不够，过于干燥，则模板吸水量大，引起混凝土的塑性收缩，产生裂缝。
1.3.2 混凝土浇捣后过分抹干压光会使混凝土的细骨料过多地浮到表面，形成含水量很大的水泥浆层，水泥浆中的氢氧化钙与空气中二氧化碳作用生成碳酸钙，引起表面体积碳水化收缩，导致混凝土板表面龟裂。
1.3.3 施工工艺不当引起：在施工过程中因施工工艺不当，致使支座处负筋下陷，保护层过大，固定支座变成塑性铰支座，使板上部沿梁支座处产生裂缝；楼板的弹性变形及支座处的负弯矩施工中在混凝土未达到规定强度，过早拆模，或者在混凝土未达到终凝时间就上荷载，造成混凝土楼板的弹性变形，致使砼早期强度低或无强度时，承受弯､压､拉应力，导致楼板产生内伤或断裂；大梁两侧的楼板不均匀沉降也会使支座产生负穹矩造成横向裂缝。
1.3.4 后浇带施工不慎而造成的板面裂缝：为了解决钢筋混凝土收缩变形和温度应力，规范要求采用施工后浇带法，有些施工后浇带不完全按设计要求施工，例如施工未留企口缝；板的后浇带不支模板，造成斜坡搓；疏松混凝土未彻底凿除等都可能造成板面的裂缝。
1.3.5 楼面垫层内铺设的暗装水管､电线套管铺设不当，如水管､电线套管铺设不够牢靠､集中铺设､上下交叠铺设致使水管､电线套管上皮在垫层厚度1/3以内，保护层厚度不足都可能造成板面沿管线长度方向产生裂缝。
1.3.6 混凝土的收缩(温度裂缝)：众所周知，混凝土引起收缩的原因，在硬化初期主要是由于水泥的水化作用，形成一种新的水泥结晶体，这种结晶体化合物较原材料体积小，因而引起混凝土体积的收缩，即所谓的凝缩，后期主要是混凝土内自由水蒸发而引起的干缩。如施工发生在夏季炎热气温下，石子表面温度升高，使石子体积膨胀，拌制成混凝土后，石子受冷收缩，使混凝土表面出现发丝裂缝；混凝土浇捣后未及时浇水养护，混凝土在较高温度下失水收缩，水化热释放量较大，而又未及时得到水分的补充，因而在硬化过程中，现浇板受到支座的约束，势必产生温度应力而出现裂缝。另外，室内外温差变化较大，也要引起一定的裂缝。
1.3.7 目前在主体结构的施工过程中，普遍存在着质量与工期之间的较大矛盾。一般主体结构的楼层施工速度平均为5～7天左右一层。如果养护时间短，更容易在强度不足的情况下受材料吊卸冲击振动荷载的作用而引起不规则的受力裂缝。而这些裂缝一旦形成，就难于闭合，形成永久性裂缝。
2 裂缝的预防措施
虽然钢筋混凝土现浇板在使用过程中，存在出现裂缝这一重大缺陷，但它与预制板相比，还是优点要大于其缺点的，它的这一缺点在设计与施工过程中，可以通过一定的措施，将其控制在规范允许的范围内。现浇板的优点主要表现在结构性能方面，采用现浇板后，将使楼､屋盖的结构刚度及强度､建筑物的整体抗震性能得到显著的提高。
对于现浇板的裂缝问题，可以采取以下几个方面的措施，以减少或避免这些裂缝的出现：
2.1 混凝土原材料质量方面
2.1.1 认真对水泥标号及安定性进行试验。
2.1.2 采取严把原材料进货关､认真地对进场砂石骨料进行检验，严格控制砂的粒径及含泥量。
2.1.3 严格控制混凝土施工配合比。根据混凝土强度等级和质量检验以及混凝土和易性的要求确定配合比，严格控制水和水泥用量，选择级配良好的石子，减小空隙率和砂率以减少收缩量，提高混凝土抗裂强度。
2.2 设计方面
2.2.1 对于地基的不均匀沉降，可以通过调整基础的选型来对楼房沉降和沉降差进行控制。
2.2.2 在板角增加辐射筋。现浇板的四周在设计上都已配置负筋，但针对绝大多数裂缝产生于板角这一现象，在板角四周增设辐射筋，使产生裂缝的应力作用方向与辐射筋相一致，能有效地抑制裂缝。
2.2.3 平面布置上尽量减少凹凸现象和设置必要的伸缩缝。平面转角过多，即薄弱部位越多，而这些部位由于应力集中，往往是裂缝的多发区。
2.3 施工质量
2.3.1 在混凝土浇捣前，应先将基层和模板浇水湿透，避免过多吸收水分，浇捣过程中应尽量做到既振捣充分又避免过度。
2.3.2 混凝土楼板浇筑完毕后，表面刮抹应限制到最小程度，防止在混凝土表面撒干水泥刮抹，并加强混凝土早期养护。防止强风和烈日曝晒。
2.3.3 严格施工操作程序，不盲目赶工。杜绝过早上传､上荷载和过早拆模。通过在大梁两侧的面层内配置通长的钢筋网片，承受支座负弯矩，避免因不均匀沉降而产生的裂缝。
2.3.4 施工后浇带的施工应认真领会设计意图，制定施工方案，杜绝在后澆处出现混凝土不密实､不按图纸要求留企口缝等现象。同时更要杜绝在未浇注混凝土前就将部分模板，支柱拆除而导致梁板形成悬臂，造成变形。
2.3.5 为避免电预埋管处裂缝，对于较粗的线管或多根线管的集散处，可增设垂直于线管的抗裂短钢筋网加强，抗裂短钢筋采用Φ6-Φ8，间距≤150，两端的锚固长度应不小于300毫米。施工时必须保证保护层达到规范规定的要求。
2.3.6 对计划中的临时大开间面积材料吊卸堆放区域部位的模板支撑架在搭设前，就预先考虑采用加密立杆和搁栅增加模板支撑架刚度的加强措施，以增强刚度，减少变形来加强该区域的抗冲击振动荷载，并应在该区域的新筑砼表面上铺设旧木模加以保护和扩散应力，进一步防止裂缝的发生。
2.3.7 加强对楼面砼的养护：砼的保湿养护对其强度增长和各类性能的提高十分重要，特别是早期的妥善养护可以避免表面脱水并大量减少砼初期伸缩裂缝发生。因此，施工中必须坚持覆盖麻袋或草包进行一周左右的妥善保湿养护，并可采用喷养护液进行养护，达到降低成本和提高工效。
2.3.8 严格控制板面负筋的保护层厚度：现浇板负筋一般放置在支座梁钢筋上面，与梁筋应绑扎在一起；另外，采用铁架子或混凝土垫块等措施来固定负筋的位置，保证在施工过程中板面钢筋不再下沉，板的保护层厚度不应大于1.5cm。
3 裂缝的处理方法
3.1 对于一般混凝土楼板表面的龟裂，可先将裂缝清洗干净，待干燥后用环氧浆液灌缝或用表面涂刷封闭。施工中若在终凝前发现龟裂时，可用抹压一遍处理。
3.2 其它一般裂缝处理，可将板缝清洗后用1：2或1：l水泥砂浆抹缝，压平养护。
3.3 当裂缝较大时，应沿裂缝凿八字形凹槽，冲洗干净后，用1：2水泥砂浆抹平，也可以采用环氧胶泥嵌补。
3.4 当楼板出现裂缝面积较大时，应对楼板进行静载试验，检验其结构安全性，必要时可在楼板上增做一层钢筋网片，以提高板的整体性。
3.5 通长､贯通的危险结构裂缝，裂缝宽度大于0.3mm的，可采用结构胶粘扁钢加固补强，板缝用灌缝胶高压灌胶。
4 结束语
对于楼屋面现浇板容易出现的一些非结构性裂缝现象，经国内外众多专家的分析研究，以及实际工程中的防治､处理案例，已经积累了比较丰富的经验。但要彻底消除裂缝现象，尚有待不断提高施工技术和进行技术创新，采用更为科学的解决方法。
参考文献
[1] 中国建筑工程总公司.地基与基础施工工艺标准[M].北京：中国建筑工业出版社，2003-11
[2] 中国建筑科学研究院 建筑地基基础设计规范北京：中国建筑工业出版社，2002-4
[3] 唐业清.简明地基基础设计施工手册.北京：中国建筑工业出版社，2003
[4] 贾宏俊､李清立.建设工程技术与计量.北京：中国计划出版社，2006-4
[5] 建筑建筑工程施工质量验收规范汇编.北京：中国建筑工业出版社，2003-4
【关键词】楼面；裂缝；分析
By floor concrete present pour liquid on board quality question and preventing and controlling measure
Zhang Xuemei
【Abstract】A few years ago the housing construction， prefabricated reinforced concrete masonry structure constitutes an important component housing， Since its construction in the presence of some fatal flaw， that is integrated seismic and poor， Therefore， in recent years it gradually residential buildings are cast-in-place reinforced concrete plate has been replaced. Along with cast-in-place reinforced concrete plate at the building housing the massive promotion and application “Residential building of cast-in-place slab cracks” became residential quality to bring complaints hot. This paper mainly from the construction， design and material balance reason for the analysis of the floor cracks comprehensive prevention and control measures.
【Key words】Floor；Crack；Analysis
【中圖分类号】TU50【文献标识码】B【文章编号】1005-250X(2008)01-0044-03
1 钢筋混凝土现浇板裂缝原因的分析
一般情况下，楼面裂缝表现为：表面龟裂，纵向､横向裂缝以及斜向裂缝。主要有设计､混凝土原材料及施工等三方面的原因。
1.1 设计方面
1.1.1 地基的不均匀沉降：在住宅建设中，有相当一部分的钢筋混凝土现浇板的裂缝，是由于地基不均匀沉降的原因而造成的。如在软土地基下采用扩展基础，则对于那些相对较长的条式楼来说，要想保正它们沉降均匀是相当困难的，因此，有时也会由于基础的不均匀沉降，而引起楼房的拉裂和钢筋混凝土现浇板的开裂。
1.1.2 荷载的作用：在住宅建设中，也有少部分钢筋混凝土现浇板的裂缝，是由于荷载作用方面的原因引起的。由于设计人员在进行现浇板的配筋计算过程中，通常只是根据其承载能力来确定配筋量的，而往往忽略了对板在正常使用阶段，其承受的荷载而引起的挠度及裂缝宽度的验算，故而引起裂缝的产生，这些裂缝有时也会超过规范的最大允许值，这也应当引起足够的重视。
1.1.3 结构体型突变及未设置必要的伸缩缝：房屋长度过长，而又未考虑设置伸缩缝，当房屋的自由伸缩达到应设置伸缩缝要求的间距时，就要引起裂缝的产生。另外，平面布局凹凸较多，即转角越多，一受到混凝土收缩及温差变化易于产生裂缝。
1.1.4 在楼房的设计中，设备专业特别是电气专业，大多将照明､有线电视､通讯等所需的管线直接敷设于现浇板中，而且有时集中于某一处现浇板中的管线多达7-8根，并且这些管线的直径多为2-3cm，由此就会使该处的现浇板厚度大大削弱，从而引起现浇板在该处开裂。
1.2 混凝土原材料质量方面
1.2.1 水泥凝结或膨胀不正常，如水泥安定性不稳定，水泥中含有生石灰或氧化镁，这些成分在和水化合后产生体积膨胀，产生裂缝。
1.2.2 如果骨料中含泥量过多，则随着混凝土的干燥，会产生不规则的网状裂缝。
1.2.3 碱——骨料反应：蛋白质､安山岩､玄武岩､辉绿岩等碱性骨料有可能与碱性很强的水泥起化学反应，生成有膨胀能力的碱——硅凝胶而引起混凝土膨胀破坏，产生裂缝。
1.2.4 水灰比､塌落度过大或使用过量粉砂混凝上强度值对水灰比的变化十分敏感，基本上是水和水泥计量变动对强度影响的叠加。因此，水､水泥､外渗混合材料外加剂溶液的计量偏差，将直接影响混凝土的强度。如采用含泥量大的粉砂配制的混凝土收缩大，抗拉强度低，容易因塑性收缩而产生裂缝。
1.3 施工质量方面
1.3.1 混凝土施工过分振捣，模板､垫层过于干燥。混凝土浇筑振捣后，粗骨料沉落挤出水分､空气，表面呈现泌水而形成竖向体积缩小沉落，造成表面砂浆层，它比下层混凝土有较大的干缩性能，待水分蒸发后，易形成凝缩裂缝。而模板､垫层在浇筑混凝上之间洒水不够，过于干燥，则模板吸水量大，引起混凝土的塑性收缩，产生裂缝。
1.3.2 混凝土浇捣后过分抹干压光会使混凝土的细骨料过多地浮到表面，形成含水量很大的水泥浆层，水泥浆中的氢氧化钙与空气中二氧化碳作用生成碳酸钙，引起表面体积碳水化收缩，导致混凝土板表面龟裂。
1.3.3 施工工艺不当引起：在施工过程中因施工工艺不当，致使支座处负筋下陷，保护层过大，固定支座变成塑性铰支座，使板上部沿梁支座处产生裂缝；楼板的弹性变形及支座处的负弯矩施工中在混凝土未达到规定强度，过早拆模，或者在混凝土未达到终凝时间就上荷载，造成混凝土楼板的弹性变形，致使砼早期强度低或无强度时，承受弯､压､拉应力，导致楼板产生内伤或断裂；大梁两侧的楼板不均匀沉降也会使支座产生负穹矩造成横向裂缝。
1.3.4 后浇带施工不慎而造成的板面裂缝：为了解决钢筋混凝土收缩变形和温度应力，规范要求采用施工后浇带法，有些施工后浇带不完全按设计要求施工，例如施工未留企口缝；板的后浇带不支模板，造成斜坡搓；疏松混凝土未彻底凿除等都可能造成板面的裂缝。
1.3.5 楼面垫层内铺设的暗装水管､电线套管铺设不当，如水管､电线套管铺设不够牢靠､集中铺设､上下交叠铺设致使水管､电线套管上皮在垫层厚度1/3以内，保护层厚度不足都可能造成板面沿管线长度方向产生裂缝。
1.3.6 混凝土的收缩(温度裂缝)：众所周知，混凝土引起收缩的原因，在硬化初期主要是由于水泥的水化作用，形成一种新的水泥结晶体，这种结晶体化合物较原材料体积小，因而引起混凝土体积的收缩，即所谓的凝缩，后期主要是混凝土内自由水蒸发而引起的干缩。如施工发生在夏季炎热气温下，石子表面温度升高，使石子体积膨胀，拌制成混凝土后，石子受冷收缩，使混凝土表面出现发丝裂缝；混凝土浇捣后未及时浇水养护，混凝土在较高温度下失水收缩，水化热释放量较大，而又未及时得到水分的补充，因而在硬化过程中，现浇板受到支座的约束，势必产生温度应力而出现裂缝。另外，室内外温差变化较大，也要引起一定的裂缝。
1.3.7 目前在主体结构的施工过程中，普遍存在着质量与工期之间的较大矛盾。一般主体结构的楼层施工速度平均为5～7天左右一层。如果养护时间短，更容易在强度不足的情况下受材料吊卸冲击振动荷载的作用而引起不规则的受力裂缝。而这些裂缝一旦形成，就难于闭合，形成永久性裂缝。
2 裂缝的预防措施
虽然钢筋混凝土现浇板在使用过程中，存在出现裂缝这一重大缺陷，但它与预制板相比，还是优点要大于其缺点的，它的这一缺点在设计与施工过程中，可以通过一定的措施，将其控制在规范允许的范围内。现浇板的优点主要表现在结构性能方面，采用现浇板后，将使楼､屋盖的结构刚度及强度､建筑物的整体抗震性能得到显著的提高。
对于现浇板的裂缝问题，可以采取以下几个方面的措施，以减少或避免这些裂缝的出现：
2.1 混凝土原材料质量方面
2.1.1 认真对水泥标号及安定性进行试验。
2.1.2 采取严把原材料进货关､认真地对进场砂石骨料进行检验，严格控制砂的粒径及含泥量。
2.1.3 严格控制混凝土施工配合比。根据混凝土强度等级和质量检验以及混凝土和易性的要求确定配合比，严格控制水和水泥用量，选择级配良好的石子，减小空隙率和砂率以减少收缩量，提高混凝土抗裂强度。
2.2 设计方面
2.2.1 对于地基的不均匀沉降，可以通过调整基础的选型来对楼房沉降和沉降差进行控制。
2.2.2 在板角增加辐射筋。现浇板的四周在设计上都已配置负筋，但针对绝大多数裂缝产生于板角这一现象，在板角四周增设辐射筋，使产生裂缝的应力作用方向与辐射筋相一致，能有效地抑制裂缝。
2.2.3 平面布置上尽量减少凹凸现象和设置必要的伸缩缝。平面转角过多，即薄弱部位越多，而这些部位由于应力集中，往往是裂缝的多发区。
2.3 施工质量
2.3.1 在混凝土浇捣前，应先将基层和模板浇水湿透，避免过多吸收水分，浇捣过程中应尽量做到既振捣充分又避免过度。
2.3.2 混凝土楼板浇筑完毕后，表面刮抹应限制到最小程度，防止在混凝土表面撒干水泥刮抹，并加强混凝土早期养护。防止强风和烈日曝晒。
2.3.3 严格施工操作程序，不盲目赶工。杜绝过早上传､上荷载和过早拆模。通过在大梁两侧的面层内配置通长的钢筋网片，承受支座负弯矩，避免因不均匀沉降而产生的裂缝。
2.3.4 施工后浇带的施工应认真领会设计意图，制定施工方案，杜绝在后澆处出现混凝土不密实､不按图纸要求留企口缝等现象。同时更要杜绝在未浇注混凝土前就将部分模板，支柱拆除而导致梁板形成悬臂，造成变形。
2.3.5 为避免电预埋管处裂缝，对于较粗的线管或多根线管的集散处，可增设垂直于线管的抗裂短钢筋网加强，抗裂短钢筋采用Φ6-Φ8，间距≤150，两端的锚固长度应不小于300毫米。施工时必须保证保护层达到规范规定的要求。
2.3.6 对计划中的临时大开间面积材料吊卸堆放区域部位的模板支撑架在搭设前，就预先考虑采用加密立杆和搁栅增加模板支撑架刚度的加强措施，以增强刚度，减少变形来加强该区域的抗冲击振动荷载，并应在该区域的新筑砼表面上铺设旧木模加以保护和扩散应力，进一步防止裂缝的发生。
2.3.7 加强对楼面砼的养护：砼的保湿养护对其强度增长和各类性能的提高十分重要，特别是早期的妥善养护可以避免表面脱水并大量减少砼初期伸缩裂缝发生。因此，施工中必须坚持覆盖麻袋或草包进行一周左右的妥善保湿养护，并可采用喷养护液进行养护，达到降低成本和提高工效。
2.3.8 严格控制板面负筋的保护层厚度：现浇板负筋一般放置在支座梁钢筋上面，与梁筋应绑扎在一起；另外，采用铁架子或混凝土垫块等措施来固定负筋的位置，保证在施工过程中板面钢筋不再下沉，板的保护层厚度不应大于1.5cm。
3 裂缝的处理方法
3.1 对于一般混凝土楼板表面的龟裂，可先将裂缝清洗干净，待干燥后用环氧浆液灌缝或用表面涂刷封闭。施工中若在终凝前发现龟裂时，可用抹压一遍处理。
3.2 其它一般裂缝处理，可将板缝清洗后用1：2或1：l水泥砂浆抹缝，压平养护。
3.3 当裂缝较大时，应沿裂缝凿八字形凹槽，冲洗干净后，用1：2水泥砂浆抹平，也可以采用环氧胶泥嵌补。
3.4 当楼板出现裂缝面积较大时，应对楼板进行静载试验，检验其结构安全性，必要时可在楼板上增做一层钢筋网片，以提高板的整体性。
3.5 通长､贯通的危险结构裂缝，裂缝宽度大于0.3mm的，可采用结构胶粘扁钢加固补强，板缝用灌缝胶高压灌胶。
4 结束语
对于楼屋面现浇板容易出现的一些非结构性裂缝现象，经国内外众多专家的分析研究，以及实际工程中的防治､处理案例，已经积累了比较丰富的经验。但要彻底消除裂缝现象，尚有待不断提高施工技术和进行技术创新，采用更为科学的解决方法。
参考文献
[1] 中国建筑工程总公司.地基与基础施工工艺标准[M].北京：中国建筑工业出版社，2003-11
[2] 中国建筑科学研究院 建筑地基基础设计规范北京：中国建筑工业出版社，2002-4
[3] 唐业清.简明地基基础设计施工手册.北京：中国建筑工业出版社，2003
[4] 贾宏俊､李清立.建设工程技术与计量.北京：中国计划出版社，2006-4
[5] 建筑建筑工程施工质量验收规范汇编.北京：中国建筑工业出版社，2003-4