据“铁钢”,№10(1984)报道:过去,川崎制铁水岛制铁所,在热精轧机前段用的是半钢工作辊。当轧制条件恶化时,轧辊表面损伤比较严重,因此改用了高铬轧辊。从现在使用情况看,没有出现任何问题,不过,为了今后更好地继续使用这种轧辊,有必要掌握辊材的基本特性—高温磨损特性。因此,采用轧辊磨损模拟装置对高铬轧辊的高温磨损特性进行了研究,并且与半钢轧辊作了对比。 According to “Iron and Steel”, № 10 (1984) reports: In the past, Kawasaki Steel Mizushima Iron Works, in the hot finishing mill before the use of semi-steel work roll. When the rolling conditions deteriorate, the roller surface damage more serious, so the use of high-chromium roll. There are no problems with the current usage, but it is necessary to grasp the basic characteristics of the roll material, high-temperature wear characteristics, in order to continue to use the roll better in the future. Therefore, the high-temperature wear characteristics of high-chromium roll were studied by the roll wear simulator and compared with the semi-steel roll.