The influence of lattice misfit on the occupation behavior and the ductility effect of Zr in Ni—Ni_3AI alloys were explored.It is found in energy analysis that the preferable site of Zr between Ni sublattice and Al sublattice will change under different lattice misfit,however,the Zr prefers to segregate Ni phase rather than Ni_3AI phase in all lattice misfit range,which makes it impossible for Zr to go into Ni_3AI phase to occupy Al sublattice in Ni—Ni_3AI system.Bond order(BO)analysis shows that the localized ductility effect of Zr differs in different region,and the comparison between Zr-free and Zr-doped BO analysis successfully explain the mechanism of the embrittlement of Ni—Ni_3AI alloys and the ductility effect of Zr.
The influence of lattice misfit on the occupation behavior and the ductility effect of Zr in Ni-Ni_3AI alloys were explored. It is found in energy analysis that the preferred site of Zr between Ni sublattice and Al sublattice will change under different lattice misfit, however, the Zr prefers to segregate Ni phase rather than Ni_3AI phase in all lattices misfit range, which makes it impossible for Zr to go into Ni_3AI phase to occupy Al sublattice in Ni-Ni_3AI system. Order (BO) analysis shows that the localized ductility effect of Zr different in different regions, and the comparison between Zr-free and Zr-doped BO analysis successfully explain the mechanism of the embrittlement of Ni-Ni_3AI alloys and the ductility effect of Zr.