变形铝合金半固态模锻成形件热处理新工艺探索

来源 :热加工工艺 | 被引量 : 0次 | 上传用户:ainyli
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
根据变形铝合金的热处理原理及其半固态模锻成形特点,探索出一种适合于变形铝合金半固态模锻成形件“高温固溶处理+分级时效”的新工艺:固溶处理(500±5)℃×25 min,分级时效140℃×6 h+150℃×1 h。结果表明:变形铝合金半固态模锻成形件经新工艺处理后,力学性能明显提高,缩短了处理时间,节约了能源,提高了生产效率。 According to the heat treatment principle of the deformed aluminum alloy and its semi-solid forging forming characteristics, a new technology suitable for semi-solid die forging deformation aluminum alloy “high temperature solution treatment + graded aging” is explored: solution treatment 500 ± 5) ℃ × 25 min, the classification aging 140 ℃ × 6 h + 150 ℃ × 1 h. The results show that the mechanical properties of the semi-solid die forging deformation parts of aluminum alloy after the new process are improved, the processing time is shortened, the energy is saved, and the production efficiency is improved.
其他文献
目的探讨胆汁返流性胃炎病因、发病机制与Hp感染的关系。方法电子胃镜下观察返流程度及Hp检测。结果Ⅰ度胆汁返流49例;Ⅱ度胆汁返流51例;Ⅲ度胆汁返流44例,幽门螺杆菌感染35
淋巴转移是乳腺癌重要的转移途径之一,有无淋巴结转移以及淋巴结转移的状况是判断患者预后的重要因素。因此,研究影响乳腺癌淋巴转移的因素,了解乳腺癌的生物学行为,对乳腺癌
对金属材料进行深冷处理,进而改善材料的力学性能,并可使其耐磨性能大大提高。在这一研究的基础上,探索金属材料深冷处理技术的扩展与应用,通过对砂砖型模深冷处理工艺的研究
多形性腺瘤是涎腺最常见的肿瘤,腮腺是多形性腺瘤最好发的部位。我科自1997年6月-2009年9月共收治130例发生于腮腺的多形性腺瘤,我们对其进行临床分析,并对手术后出现的并发
研究了双级固溶和双级时效对Al-Si-Mg合金组织、硬度和耐磨性的影响。结果表明:经520℃固溶8 h,然后再经145℃预时效3.5h和175℃终时效3.5h热处理后的试样硬度高,耐磨性好。
采用快速加热模拟电脉冲引起的焦耳热效应,研究了快速加热处理对冷轧态AZ31镁合金组织与力学性能的影响。结果表明:快速加热处理能实现较低温度下的快速完全再结晶,并在不牺
6包装和贮运卫生  6.1包装  包装物料应符合相关标准,不应含有有毒有害物质,不应改变肉的感官特性。包装材料应有足够的强度,保证在运输和搬运过程中不破损。  6.2贮存 
采用共沉淀法制备固体超强酸SO2-4/TiO2/La3+,并通过十四酸正丁酯酯化反应的酯化率考察催化剂制备因素对催化活性的影响.结果表明固体超强酸SO2-4/TiO2/La3+催化剂的最佳制备
用SEM、金相分析及力学性能测试研究了12Cr1 MoV钢在550℃保温不同时间后的微观组织和性能.结果表明:随保温时间的延长,12Cr1MoV钢的抗拉强度逐渐升高;屈服强度、伸长率、断
研究了固溶处理对S31803双相钢板焊接接头微观组织的影响。结果表明:经固溶处理的焊缝和热影响区,晶内奥氏体析出变少,晶粒尺寸变小,同时奥氏体的形状由长条状变为圆状。 Th