The uniaxial ratcheting behaviors of several metals with different crystal structures or values of fault energy were observed by the stress-controlled cyclic tests at room temperature. The prescribed metals included 316L stainless steel, pure copper, pure aluminum, and ordinary 20# carbon steel. The effects of applied mean stress, stress amplitude and stress ratio on the uniaxial ratcheting were also investigated. The observations show that different crystal structures or values of fault energy result in more or less di?erent ratcheting behaviors for the prescribed metals. The different ratcheting behaviors are partially caused by the variation of dislocation mobility.
The uniaxial ratcheting behaviors of several metals with different crystal structures or values of fault energy were observed by the stress-controlled cyclic tests at room temperature. The prescribed metals included 316L stainless steel, pure copper, pure aluminum, and ordinary 20 # carbon steel. The effects of applied mean stress, stress amplitude and stress ratio on the uniaxial ratcheting were also investigated. The observations show that different crystal structures or values of fault energy result in more or less di? Erent ratcheting behaviors for the prescribed metals. The different ratcheting behaviors are partially caused by the variation of dislocation mobility