A series of CoCrFeNb_xNi(x values in molar ratio, x = 0, 0.25, 0.45, 0.5, 0.75, 1.0 and 1.2) high entropy alloys(HEAs) was prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties. The results indicate that the prepared CoCrFeNb_xNi(x > 0) HEAs consist of a simple FCC solid solution phase and a Laves phase. The microstructures of the alloys change from an initial single-phase FCC solid solution structure(x = 0) to a hypoeutectic microstructure(x = 0.25), then to a full eutectic microstructure(x = 0.45) and finally to a hypereutectic microstructure(0.5 < x < 1.2). The compressive test results show that the Nb0.45(x = 0.45) alloy with a full eutectic microstructure possesses the highest compressive fracture strength of 2558 MPa and a fracture strain of 27.9%. The CoCrFeNi alloy exhibits an excellent compressive ductility, which can reach 50% height reduction without fracture. The Nb0.25 alloy with a hypoeutectic structure exhibits a larger plastic strain of 34.8%. With the increase of Nb content, increased hard/brittle Laves phase leads to a decrease of the plasticity and increases of the Vickers hardness and the wear resistance. The wear mass loss, width and depth of wear scar of the Nb1.2(x = 1.2) alloy with a hypereutectic structure are the lowest among all alloy systems, indicating that the wear resistance of the Nb1.2 alloy is the best one.
A series of CoCrFeNb_xNi (x values in molar ratio, x = 0, 0.25, 0.45, 0.5, 0.75, 1.0 and 1.2) high entropy alloys (HEAs) was prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties. results indicate that the prepared CoCrFeNb_xNi (x> 0) HEAs consist of a simple FCC solid solution phase and a Laves phase. The microstructures of the alloys change from an initial single-phase FCC solid solution structure (x = 0) to a hypoeutectic microstructure (x = 0.45) and finally to a hypereutectic microstructure (0.5
其他文献
请下载后查看,本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
随着钻完井技术的不断发展,自膨胀封隔器技术已经越来越广泛地应用于水平井分段开采、低渗透储层和页岩气储层分段压裂等领域.由于不同井况及施工工艺对封隔器的封压时间和封
2001年3月,我在布宜诺斯艾利斯亲身经历了那一场经济浩劫。许多店铺的大门上都挂出了“闭门歇业”的牌子;出租车司机们喋喋不休地诉说着国家的巨大困境,用词夸张;各大主流报
【本刊讯】2016年12月24—25日,由国家发展和改革委员会中国经贸导刊杂志社、中国发展网主办,中金国研信息技术研究院承办,中金国研智库提供学术支持的“2017中国宏观经济高
利用SEM、EPMA、XRD、DSC对Nb-Ni-Ti系低Ni侧1000℃的液相相关相平衡进行了研究。结果表明,1000℃时,在Nb-Ni-Ti系低Ni侧存在着一个可与(Nb,bTi)连续固溶体和TiNi化合物相平
页岩气藏大规模加砂压裂后地面连续返排测试作业以及钻塞冲砂作业期间,返排液含大量砂粒和碎屑,地面返排测试流程易发生堵塞或刺漏,安全风险高.本文针对上述问题,完善地面流
会议
请下载后查看,本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
水平井裸眼分段压裂技术是将完井管柱和压裂管柱合并为一趟管柱一起下入.采用悬挂封隔器悬挂裸眼封隔器、压力开启滑套、投球开启滑套等工具下入井内.使用裸眼封隔器封隔水平
会议