摘要：我国当前许多已有建筑没有达到规定的抗震标准，在地震发生时，房屋易遭破坏，给人们带来巨大的经济损失，威胁生命安全。因此,对房屋的抗震加固改造技术的研究一直是抗震加固工作的重点。本文分析了抗震加固的原则，重点介绍了植筋加固技术和碳纤维加固技术，浅略分析了增设扶壁柱和现浇钢筋混凝土板墙加固墙体在房屋抗震加固中的应用。
关键词：植筋加固；碳纤维加固；增设扶壁柱
Abstract: the present many existing buildings did not meet the prescribed standards for earthquake, the earthquake occurs, the housing vulnerable to destruction, bring huge economic losses, the threat to life. Therefore, the building seismic strengthening technical transformation of the research is always the key point of the seismic strengthening work. This paper analyzes the seismic strengthening principle, focus on plant steel reinforcement technique and technology of carbon fiber reinforced plastics, slightly shallow analysis the additional help pilaster and cast-in-place reinforced concrete wall reinforcement wall in building the application of the seismic strengthening.
Keywords: steel reinforcement; Carbon fiber reinforced plastics; Add up post
中图分类号：TU746.3文献标识码：A文章编号：2095-2104(2013)
一、房屋抗震加固的原则
抗震加固的原理是：通过对结构的构件、结构受力的途径的改善，提高结构的抗震能 力，实现结构的地震破坏有所减小。钢筋混凝土结构的抗震加固原则主要表现在以下几个方面：
1、在结构的抗震鉴定结果的基础上，才可进行结构的抗震加固。在具体的加固实施过程中可以采用整体加固、区段加固以及构建加固。2、在对加固方案进行确定时，应该深入的调查结构的现状，对结构是否存在局部损伤应特别查明，如果发现有损伤，应对这些损伤进行专门的研究。
3、在对抗震加固方案进行确定时，要对结构总体抗震能力和变形能力的综合协调进行重点考虑，以避免构件加固。
4、根据结构的实际情况，抗震加固应采用主要提高框架抗震承载能力、主要增强框架变形能力或改变结构体系而不加固框架的方案。
5、避免加固后的框架形成短柱、短梁或强梁弱柱。
6、在选择加固方案时，应避免原结构的薄弱层发生转移，但是，如果转移发生，则处理新的薄弱层。
7、在增设墙体、支撑等构件时，对于结构体系的变化应该予以注意，除此之外，还应对结构内力的重分布以及可能出现的局部应力集中都应该注意。
8、安全性是抗震加固的重点，但是对于结构适用和美观应必须考虑。科学而合理的加固方案是安全和美观的有机统一。
9、在选择加固方法时，也应该考虑经济、对生产和生活的影响的问题，则应选较经济、便于施工的方法，且对生产和生活的影响也应最低。
二、植筋加固技术
植筋技术是在需连接的旧混凝土构件上根据结构的受力特点，确定钢筋的数量、规格、位置，在旧构件上经过钻孔、清孔、注入植筋粘结剂，再插入所需钢筋，使钢筋与混凝土通过结构胶粘结在一起，然后浇注新混凝土，从而完成新旧钢筋混凝土的有效连接，达到共同作用、整体受力的目的。
由于在钢筋混凝土结构上植筋锚固已不必再进行大量的开凿挖洞，而只需在植筋部位钻孔后，利用化学锚固剂作为钢筋与混凝土的粘合剂就能保证钢筋与混凝土的良好粘接，从而减轻对原有结构构件的损伤，也减少了加固改造工程的工程量，又因植筋胶对钢筋的锚固力，使锚杆与基材有效地锚固在一起，产生的粘接强度与机械咬合力来承受受拉载荷，当植筋达到一定的锚固深度后，植入的钢筋就具有很强的抗拉力，从而保证了锚固强度。作为一种新型的加固技术，植筋技术不仅具有有方便、工作面小、工作效率高的特点，而且还具有适应性强、适用范围广、锚固结构的整体性能良好、价格低廉等优点。因此被广泛应用于建筑结构加固及混凝土的补强工程中。在现代住宅建筑中也使用植筋技术进行加固。
植筋技术在已有的现代住宅建筑加固及改造工程中的应用，主要有以下几种形式：
1、在原有结构上增加新构件，改变原有结构的布置和形式，如新增梁、柱 。
2、增大原有结构构件的截面尺寸。
3、改变原有混凝土结构构件的约束条件和受力特征。
4、充当预埋件和锚栓的作用。
三、碳纤维加固技术
碳纤维加固包括碳纤维布加固和碳纤维板加固两种。碳纤维加固是将抗拉强度极高的碳纤维用环氧树脂预浸成为复合增强材料（单向连续纤维）；用环氧树脂粘结剂沿受拉方向或垂直于裂缝方向粘贴在要补强的结构上，形成一个新的复合体，使增强粘贴材料与原有钢筋混凝土共同受力增大结构的抗裂或抗剪能力，提高结构的强度、刚度、抗裂性和延伸性。碳纤维加固技术施工要点如下：
（一） 混凝土表面处理
1、将混凝土构件表面的残缺、破损部分清除干净。
2、对经过剔凿、清理和露筋的构件残缺部分，进行修补、复原。
3、裂缝修补：缝宽小于0.2mm的裂缝，用环氧树脂进行表面涂刷密封；大于0.2mm的裂缝用环氧树脂灌缝。
4、打磨：将构件表面凸出部分（混凝土构件交接部位、模板的接槎等）打磨平整，修复后的构件表面尽量平顺。
5、清洗打磨过的构件表面，并使其充分干燥。
（二）缺陷部位涂刷底胶
将配好的底胶（粘结剂），用涂刷均匀于缺陷部位的砼表面。
（三）构件表面残缺面的修补
用环氧腻子对构件表面残缺面的修补是十分重要的一步，要点如下：
1、腻子主剂、固化催进剂、固化剂按规定比例称量准确，装入容器，用搅拌器搅拌均匀。
2、构件表面凹陷部位用环氧腻子填平，修复至表面平整。在残缺修补中使用环氧腻子时，要在气温-5℃以上，相对湿度小于85%的条件下施工。腻子涂刮后，表面仍存在的凹凸糙纹，应再用砂纸打磨平整。
（四）涂刷底胶
將配好的底胶（粘结剂），用滚筒均匀涂刷于需要粘结的砼表面。
（五）粘贴碳纤维
粘贴碳纤维材料之前，首先应确认粘贴表面干燥。气温在-10℃以上，相对湿度RH>85%时，如无有效措施不得施工。为防止碳纤维受损，在碳纤维材料运输、储存、裁切和粘贴过程中。应用钢直尺与壁纸刀按规定尺寸切断碳纤维材料，每段长度一般以不超过6m为宜。为防止材料在保管过程中损坏，材料的裁切数量应按当天的用量裁切为准。碳纤维纵向接头必须搭接20cm以上。该部位应多涂树脂，碳纤维横向不需要搭接。其施工工艺要点如下：
1、 粘贴树脂的主剂、固化催促剂和固化剂应按规定的比例称量准确，装入容器，用搅拌器搅拌均匀。一次调和量应以在可使用时间内用完为准。
2、粘贴时，在碳纤维和树脂之间尽量不要有空气。可用罗拉（专用工具）沿着纤维方向在碳纤维材料上滚压多次，使树脂渗浸入碳纤维中。
（六）养护
粘贴碳纤维材料后，需自然养护1-2小时达到初期固化，应保证固化期间不受外界干扰和碰撞。
（七） 涂装
若加固补强构件需要防火时，可在树脂固化后涂刷耐火涂层。涂装应在树脂初期固化后进行，并应遵守所用涂料的相关标准和施工规定。
四、现浇钢筋混凝土板墙加固墙体
利用现浇钢筋砼板墙加固砖砌体时,混凝土与砖砌体的弹性模量相差较大,混凝土不能充分发挥作用,其强度等级不宜过高,厚度不宜过大。为使板墙加固有效,应注意以下问题:
1、板墙与原有楼板、周边结构构件应可靠连接。采用短筋与上下楼板连接时,短筋在板墙内的锚固长度不小于40倍短筋直径。板墙与两端原有墙体连接可沿墙高每隔017～110m设2Φ12的拉结钢筋。
2、板墙的钢筋应与原砖墙锚固。
3、板墙应有基础。条件允许时,基础埋深同原有基础。
五、增设扶壁柱加固技术
该技术属于加大截面加固法的一种，其优点与钢筋混凝土外加层加固法相近，但承载力提高有限，且较难满足抗震要求，一般在非地震地区应用，它属于砌体结构的间接加固方法。一般有两种做法，第一种为无黏结外包型钢加固法，该法属于传统加固方法，其优点是：施
工简便、现场工作量和湿作业少，受力较为可靠，适用于不允许增大原构件截面尺寸，却又要求大幅度提高截面承载力的砌体柱的加固；其缺点为：加固费用较高，并需采用类似钢结构的防护措施；第二种为预应力撑杆加固法，其优点是：能较大幅度地提高砌体柱的承载能力，且加固效果可靠，适用于加固处理高应力、高应变状态的砌体结构的加固；其缺点是不能用于温度在600℃以上的环境中。
参考文献
[1]混凝土结构加固设计规范GB50367-2006．
[2]杨威，王力波 某多层砌体房屋改造及抗震加固设计[J].建筑结构,2010(12).
[3]谷军明,缪昇.对砌体结构抗震加固探讨[C].抗震加固改造技术第一届学术交流会论文集，2004.
[4]刘迪，宋晓胜．化学植筋技术应用中应注意的几个问题[J]．四川建材，2009(1).
[5]郭俊雄．浅談植筋技术加固原理及施工质量的控制[J]．内江科技，2009(10).
[6]刘霁，赵国基．化学锚固技术在增建或改建工程中的应用[J]．株洲工学院学报，2001(1).
关键词：植筋加固；碳纤维加固；增设扶壁柱
Abstract: the present many existing buildings did not meet the prescribed standards for earthquake, the earthquake occurs, the housing vulnerable to destruction, bring huge economic losses, the threat to life. Therefore, the building seismic strengthening technical transformation of the research is always the key point of the seismic strengthening work. This paper analyzes the seismic strengthening principle, focus on plant steel reinforcement technique and technology of carbon fiber reinforced plastics, slightly shallow analysis the additional help pilaster and cast-in-place reinforced concrete wall reinforcement wall in building the application of the seismic strengthening.
Keywords: steel reinforcement; Carbon fiber reinforced plastics; Add up post
中图分类号：TU746.3文献标识码：A文章编号：2095-2104(2013)
一、房屋抗震加固的原则
抗震加固的原理是：通过对结构的构件、结构受力的途径的改善，提高结构的抗震能 力，实现结构的地震破坏有所减小。钢筋混凝土结构的抗震加固原则主要表现在以下几个方面：
1、在结构的抗震鉴定结果的基础上，才可进行结构的抗震加固。在具体的加固实施过程中可以采用整体加固、区段加固以及构建加固。2、在对加固方案进行确定时，应该深入的调查结构的现状，对结构是否存在局部损伤应特别查明，如果发现有损伤，应对这些损伤进行专门的研究。
3、在对抗震加固方案进行确定时，要对结构总体抗震能力和变形能力的综合协调进行重点考虑，以避免构件加固。
4、根据结构的实际情况，抗震加固应采用主要提高框架抗震承载能力、主要增强框架变形能力或改变结构体系而不加固框架的方案。
5、避免加固后的框架形成短柱、短梁或强梁弱柱。
6、在选择加固方案时，应避免原结构的薄弱层发生转移，但是，如果转移发生，则处理新的薄弱层。
7、在增设墙体、支撑等构件时，对于结构体系的变化应该予以注意，除此之外，还应对结构内力的重分布以及可能出现的局部应力集中都应该注意。
8、安全性是抗震加固的重点，但是对于结构适用和美观应必须考虑。科学而合理的加固方案是安全和美观的有机统一。
9、在选择加固方法时，也应该考虑经济、对生产和生活的影响的问题，则应选较经济、便于施工的方法，且对生产和生活的影响也应最低。
二、植筋加固技术
植筋技术是在需连接的旧混凝土构件上根据结构的受力特点，确定钢筋的数量、规格、位置，在旧构件上经过钻孔、清孔、注入植筋粘结剂，再插入所需钢筋，使钢筋与混凝土通过结构胶粘结在一起，然后浇注新混凝土，从而完成新旧钢筋混凝土的有效连接，达到共同作用、整体受力的目的。
由于在钢筋混凝土结构上植筋锚固已不必再进行大量的开凿挖洞，而只需在植筋部位钻孔后，利用化学锚固剂作为钢筋与混凝土的粘合剂就能保证钢筋与混凝土的良好粘接，从而减轻对原有结构构件的损伤，也减少了加固改造工程的工程量，又因植筋胶对钢筋的锚固力，使锚杆与基材有效地锚固在一起，产生的粘接强度与机械咬合力来承受受拉载荷，当植筋达到一定的锚固深度后，植入的钢筋就具有很强的抗拉力，从而保证了锚固强度。作为一种新型的加固技术，植筋技术不仅具有有方便、工作面小、工作效率高的特点，而且还具有适应性强、适用范围广、锚固结构的整体性能良好、价格低廉等优点。因此被广泛应用于建筑结构加固及混凝土的补强工程中。在现代住宅建筑中也使用植筋技术进行加固。
植筋技术在已有的现代住宅建筑加固及改造工程中的应用，主要有以下几种形式：
1、在原有结构上增加新构件，改变原有结构的布置和形式，如新增梁、柱 。
2、增大原有结构构件的截面尺寸。
3、改变原有混凝土结构构件的约束条件和受力特征。
4、充当预埋件和锚栓的作用。
三、碳纤维加固技术
碳纤维加固包括碳纤维布加固和碳纤维板加固两种。碳纤维加固是将抗拉强度极高的碳纤维用环氧树脂预浸成为复合增强材料（单向连续纤维）；用环氧树脂粘结剂沿受拉方向或垂直于裂缝方向粘贴在要补强的结构上，形成一个新的复合体，使增强粘贴材料与原有钢筋混凝土共同受力增大结构的抗裂或抗剪能力，提高结构的强度、刚度、抗裂性和延伸性。碳纤维加固技术施工要点如下：
（一） 混凝土表面处理
1、将混凝土构件表面的残缺、破损部分清除干净。
2、对经过剔凿、清理和露筋的构件残缺部分，进行修补、复原。
3、裂缝修补：缝宽小于0.2mm的裂缝，用环氧树脂进行表面涂刷密封；大于0.2mm的裂缝用环氧树脂灌缝。
4、打磨：将构件表面凸出部分（混凝土构件交接部位、模板的接槎等）打磨平整，修复后的构件表面尽量平顺。
5、清洗打磨过的构件表面，并使其充分干燥。
（二）缺陷部位涂刷底胶
将配好的底胶（粘结剂），用涂刷均匀于缺陷部位的砼表面。
（三）构件表面残缺面的修补
用环氧腻子对构件表面残缺面的修补是十分重要的一步，要点如下：
1、腻子主剂、固化催进剂、固化剂按规定比例称量准确，装入容器，用搅拌器搅拌均匀。
2、构件表面凹陷部位用环氧腻子填平，修复至表面平整。在残缺修补中使用环氧腻子时，要在气温-5℃以上，相对湿度小于85%的条件下施工。腻子涂刮后，表面仍存在的凹凸糙纹，应再用砂纸打磨平整。
（四）涂刷底胶
將配好的底胶（粘结剂），用滚筒均匀涂刷于需要粘结的砼表面。
（五）粘贴碳纤维
粘贴碳纤维材料之前，首先应确认粘贴表面干燥。气温在-10℃以上，相对湿度RH>85%时，如无有效措施不得施工。为防止碳纤维受损，在碳纤维材料运输、储存、裁切和粘贴过程中。应用钢直尺与壁纸刀按规定尺寸切断碳纤维材料，每段长度一般以不超过6m为宜。为防止材料在保管过程中损坏，材料的裁切数量应按当天的用量裁切为准。碳纤维纵向接头必须搭接20cm以上。该部位应多涂树脂，碳纤维横向不需要搭接。其施工工艺要点如下：
1、 粘贴树脂的主剂、固化催促剂和固化剂应按规定的比例称量准确，装入容器，用搅拌器搅拌均匀。一次调和量应以在可使用时间内用完为准。
2、粘贴时，在碳纤维和树脂之间尽量不要有空气。可用罗拉（专用工具）沿着纤维方向在碳纤维材料上滚压多次，使树脂渗浸入碳纤维中。
（六）养护
粘贴碳纤维材料后，需自然养护1-2小时达到初期固化，应保证固化期间不受外界干扰和碰撞。
（七） 涂装
若加固补强构件需要防火时，可在树脂固化后涂刷耐火涂层。涂装应在树脂初期固化后进行，并应遵守所用涂料的相关标准和施工规定。
四、现浇钢筋混凝土板墙加固墙体
利用现浇钢筋砼板墙加固砖砌体时,混凝土与砖砌体的弹性模量相差较大,混凝土不能充分发挥作用,其强度等级不宜过高,厚度不宜过大。为使板墙加固有效,应注意以下问题:
1、板墙与原有楼板、周边结构构件应可靠连接。采用短筋与上下楼板连接时,短筋在板墙内的锚固长度不小于40倍短筋直径。板墙与两端原有墙体连接可沿墙高每隔017～110m设2Φ12的拉结钢筋。
2、板墙的钢筋应与原砖墙锚固。
3、板墙应有基础。条件允许时,基础埋深同原有基础。
五、增设扶壁柱加固技术
该技术属于加大截面加固法的一种，其优点与钢筋混凝土外加层加固法相近，但承载力提高有限，且较难满足抗震要求，一般在非地震地区应用，它属于砌体结构的间接加固方法。一般有两种做法，第一种为无黏结外包型钢加固法，该法属于传统加固方法，其优点是：施
工简便、现场工作量和湿作业少，受力较为可靠，适用于不允许增大原构件截面尺寸，却又要求大幅度提高截面承载力的砌体柱的加固；其缺点为：加固费用较高，并需采用类似钢结构的防护措施；第二种为预应力撑杆加固法，其优点是：能较大幅度地提高砌体柱的承载能力，且加固效果可靠，适用于加固处理高应力、高应变状态的砌体结构的加固；其缺点是不能用于温度在600℃以上的环境中。
参考文献
[1]混凝土结构加固设计规范GB50367-2006．
[2]杨威，王力波 某多层砌体房屋改造及抗震加固设计[J].建筑结构,2010(12).
[3]谷军明,缪昇.对砌体结构抗震加固探讨[C].抗震加固改造技术第一届学术交流会论文集，2004.
[4]刘迪，宋晓胜．化学植筋技术应用中应注意的几个问题[J]．四川建材，2009(1).
[5]郭俊雄．浅談植筋技术加固原理及施工质量的控制[J]．内江科技，2009(10).
[6]刘霁，赵国基．化学锚固技术在增建或改建工程中的应用[J]．株洲工学院学报，2001(1).