摘 要：以具有观赏价值的植物花、叶为材料，制成干燥标本，分别用环氧树脂AB胶（水晶滴胶）和新型UV滴胶进行包埋，最后固化脱模制成工艺成品，比较分析新型UV滴胶与不同操作条件下环氧树脂AB胶制作的工艺饰品效果。结果表明：沸水浴加热搅拌AB胶和恒温（40℃）固化可有效减少植物工艺饰品气泡，缩短固化时间;而采用新型UV滴胶制作几乎不产生气泡，固化时间大幅缩短，透明度高，但成本稍高。由此可见，采用环氧树脂AB膠和新型UV滴胶均可获得较佳的植物工艺饰品，具有较好的市场应用前景。
关键词：环氧树脂AB胶;UV胶;工艺饰品
中图分类号 TQ427.2 文献标识码 A 文章编号 1007-7731（2021）05-0162-03
Abstract： Plant flowers and leaves with ornamental value were used as materials to make dry specimens， which were respectively embedded with epoxy AB glue （crystal glue） and new UV glue. Finally， the finished products were cured and unmoulded. Compared and analyzed the effect of new UV glue and epoxy AB glue under different operating conditions. The results showed that boiling water bath heating， stirring AB glue and curing at a constant temperature （40℃） could effectively reduce the bubble of plant craft ornaments and shorten the curing time. The new type of UV glue produced almost no bubbles， curing time greatly shortened， high transparency， but slightly high cost. Therefore， the use of epoxy AB glue and the new type of UV glue can get better plant craft ornaments， has a higher market application prospect.
Key words： Epoxy AB glue; UV glue; Craft ornaments
随着我国经济的不断发展和国民收入的增加，女性对饰品的需求剧增[1]，尤其对手工饰品的需求日益旺盛。消费者开始追求更具有个性化、更环保、带有自然风格元素的工艺饰品。植物标本具有极高的观赏应用价值，将具有观赏价值的植物标本做成工艺饰品，深受消费者喜爱。目前植物工艺饰品主要有人造琥珀[2-3]、脲醛树脂[4]、水晶滴胶（环氧树脂AB胶）[5-7]等制作方法。水晶滴胶具有操作简单、透明度高等特点，是制作工艺饰品的较佳选择。传统水晶滴胶的制作原料主要为环氧树脂AB胶，是由环氧树脂和固化剂组成的双组分高分子材料，具有无毒、无污染、透明度高、硬度高、粘度低、成本低等优点[7]。随着化工业的迅速发展，新型滴胶材料UV胶进入大众视野。UV胶又称光敏胶、紫外光固化胶[8]，是一种通过紫外线照射实现快速固化的滴胶材料。本研究选用传统水晶滴胶与新型滴胶材料UV胶来制作植物工艺饰品，比较不同操作方法、不同胶体对工艺饰品制作效果的影响，探究水晶滴胶工艺饰品的制作方法，为其推广应用提供参考。
1 材料与方法
1.1 试验器材 DHG-9070A型电热恒温鼓风干燥箱，DenverTP-114型电子天平，36W紫外线灯（波长：365～405nm）。硅胶模具，一次性塑料分胶杯，滴胶搅拌棒，一次性塑料滴管，剪刀，标本夹，牙签。普通高透环氧树脂AB胶（硬胶），新型UV胶（硬胶）。试验所用植物材料均取自阿坝师范学院校园内，主要为植物花朵及彩叶。
1.2 试验方法
1.2.1 植物材料处理 选取健康、形态完整的植物材料，整形后置于标本夹中，上下两面均用报纸覆盖包裹，然后将其夹紧，置于50℃的恒温干燥箱中进行恒温加热快速干燥植物标本，更好地保存植物花叶的色泽和形态[9-11]。
1.2.2 植物花叶标本制作 分别采用传统环氧树脂AB胶与新型UV胶制作植物标本饰品，制作过程中记录气泡产生情况及固化时间，观察固化脱模后成品的颜色、透明度、硬度。
（1）环氧树脂AB胶混合与包埋脱模。配制滴胶：用天平分别称取适量A胶3份，然后按照一定质量比（A胶∶B胶=3∶1）称取适量的A、B胶，将A胶与B胶分别按表1的3种操作方法（C1、C2、C3）进行混合，记录气泡产生情况及固化时间。包埋脱模：将配制好的胶体先倒入模具一半的位置，把植物标本放入其中，并进行整形，使其美观。如有气泡产生，用针头或牙签将气泡挑出，静置直至气泡消失。然后分别将模具置于特定试验条件（C1、C2、C3）进行固化。待下层胶体基本能将标本固定住不再上浮，再立即配制第2份滴胶，然后进行模具空余部分的填充，待其完全凝固后进行脱模。
（2）新型UV胶包埋脱模。将植物标本放置在模具中进行整形，然后取少量UV胶涂抹于标本的不同部位，用紫外灯进行照射，将标本固定于模具内。标本固定后缓慢向模具中倒入1层UV胶，如有气泡，用牙签挑出，然后用紫外灯进行照射，待底层胶体凝固后再倒入1层UV胶，然后用紫外灯照射，重复上述操作直至填充完成。UV胶在紫外灯的照射下凝固较快，但在凝固过程中要注意少量多次倒胶，待底层胶体完全凝固后再倒下一层胶体，以防中间胶体未完全凝固导致后续出现凝固不了的现象。待胶体完全固化后进行脱模。 1.2.3 标本、饰品的后期制作 将固化好的滴胶产品进行打磨抛光和装饰，镶嵌上挂绳、金属扣等，制成精美成品。
2 结果与分析
2.1 不同制作方法的滴胶工艺饰品效果 由表2及图1可知，相较于常规操作方法（C1组），C2、C3组制作的滴胶（环氧树脂AB胶）工艺成品产生的气泡较少。在沸水浴中进行混合搅拌的C2组，在刚完成填充时产生的气泡较少或不产生气泡，但在后续凝固过程中会逐渐产生气泡，完全固化所需的时间较C1组短。水浴可降低树脂黏度，增加流动性[13]。而包埋后放置于恒温干燥箱（40℃）中固化的C3组产生的气泡最少，且固化时间最短。由此可见，40℃恒温条件能有效加快反应速度，缩短固化时间[12-13]。
2.2 不同材质滴胶制作的工艺饰品效果 使用新型UV胶制作植物工艺饰品步骤简单，完全固化所需的时间也大幅缩短，成品的透明度和硬度与环氧树脂AB胶制作的成品相当（表2、图2）。由于操作过程无需混合胶体，大大减小了气泡产生的可能性。环氧树脂AB胶制作的成品呈透明色，但UV胶在完全固化后成品胶体会微微泛黄，在制作颜色丰富的植物工艺饰品时会产生轻微的色差（图2）。
2.3 不同植物材料制作的工艺成品 通过对比植物彩叶（层次简单）和花朵（层次复杂）制成的滴胶（环氧树脂AB胶）饰品成品，发现花朵工艺饰品比叶类更容易产生气泡（图1、图2）。由于花瓣间具有空隙，直接倒胶会导致胶体不能完全填充进每一个缝隙，在缝隙间就极易产生气泡，后续凝固时气泡会受温度等影响上浮或是附着在花瓣上，影响成品的美观性。因此在制作花朵类滴胶时，可先用一次性的塑料滴管吸取少量胶体，填充进花瓣中，确保每一片花瓣都均匀涂抹上滴胶，待花瓣上的滴胶凝固后再将花朵进行整体包埋。这不仅可以减少气泡的产生，还可以在操作过程中给花瓣整姿，使花朵呈现出更好的美观性。
3 结论与讨论
试验结果表明：水浴加热混合水晶滴胶、恒温（40℃）条件下进行固化可有效缩短固化时间，减少气泡的产生，制作的水晶滴胶工艺饰品效果最佳;新型UV胶操作简单、气泡少、固化时间短，但对成品颜色稍有影响，对成品颜色有高精度要求的应不予考虑。同时，层次复杂的植物材料操作难度更大，影响水晶滴胶标本成品效果。相较于传统工艺饰品制作方法，环氧树脂AB胶与新型UV胶制作的标本具有透明度高、硬度高、操作简单等特点，可有效保存植物标本的颜色及立体姿态等。UV胶的使用更是精简了标本制作步骤，大幅缩短固化时间，减少气泡的产生，提高了成品制作的成功率。但UV胶的固化需要紫外线灯进行照射，紫外线照射空气时会产生臭氧，对人体会造成伤害[8]，而且UV胶是新型滴胶材料，价格偏高。环氧树脂AB胶通过沸水浴混合与恒温固化也能够大幅缩短时间，获得质量较高的成品，成本更为低廉。两者各有优缺点，可根据具体需求进行选择。总之，水晶滴胶与UV胶均能使植物标本高度保真，具有较高的观赏价值，有利于在立体教学标本、水晶滴胶工艺饰品制作等方面的应用。
参考文献
[1]刘杰克，金梓.中国饰品市场分析及竞争策略[J].市场研究，2006（05）：5-7.
[2]张甲敏，祝勇，陈军龙.人造琥珀的制作方法[J].河南科技学院学报（自然科学版），2008（02）：59-62.
[3]有保和.人工琥珀标本的简易制作[J].生物学通报，1996（01）：38.
[4]唐安科，唐发辉，赵元莙.一种透明水溶性树脂包埋生物标本的新方法[J].重庆师范大学学报（自然科学版），2008（01）：91-92.
[5]董禎.一种新型的水晶滴胶生成技术[J].北京农业，2015（28）：197.
[6]饶星，彭姚.大学生创新创业探索实践——“手底生花”创意滴胶项目探讨[J].品牌研究，2018（02）：118-120.
[7]张建逵，邢艳萍，李倩，等.环氧树脂AB胶制作叶、花类药用植物标本的研究[J].现代中药研究与实践，2015，29（04）：24-26.
[8]张南哲，朴哲，梁永日，等.紫外光（UV）照射固化光敏胶[J].延边大学学报（自然科学版），2000（01）：67-71.
[9]李婷.干花制作技术浅谈[J].科技资讯，2008（16）：213.
[10]李芬，吴文霖，祝剑峰.干燥花制作技术[J].安徽农学通报，2020，26（12）：37-38.
[11]兰霞，盛爱武，余晓华，等.玫瑰干燥花制作工艺研究[J].北方园艺，2011（17）：158-160.
[12]张启霄，姚亚丽，安硕，等.水晶滴胶制作昆虫标本[J].实验室科学，2018，21（05）：85-87.
[13]刘冬妮，张荣荣，孙思，等.高质量树脂标本的制作与应用[J].产业与科技论坛，2015，14：77-78. （责编：徐世红）
关键词：环氧树脂AB胶;UV胶;工艺饰品
中图分类号 TQ427.2 文献标识码 A 文章编号 1007-7731（2021）05-0162-03
Abstract： Plant flowers and leaves with ornamental value were used as materials to make dry specimens， which were respectively embedded with epoxy AB glue （crystal glue） and new UV glue. Finally， the finished products were cured and unmoulded. Compared and analyzed the effect of new UV glue and epoxy AB glue under different operating conditions. The results showed that boiling water bath heating， stirring AB glue and curing at a constant temperature （40℃） could effectively reduce the bubble of plant craft ornaments and shorten the curing time. The new type of UV glue produced almost no bubbles， curing time greatly shortened， high transparency， but slightly high cost. Therefore， the use of epoxy AB glue and the new type of UV glue can get better plant craft ornaments， has a higher market application prospect.
Key words： Epoxy AB glue; UV glue; Craft ornaments
随着我国经济的不断发展和国民收入的增加，女性对饰品的需求剧增[1]，尤其对手工饰品的需求日益旺盛。消费者开始追求更具有个性化、更环保、带有自然风格元素的工艺饰品。植物标本具有极高的观赏应用价值，将具有观赏价值的植物标本做成工艺饰品，深受消费者喜爱。目前植物工艺饰品主要有人造琥珀[2-3]、脲醛树脂[4]、水晶滴胶（环氧树脂AB胶）[5-7]等制作方法。水晶滴胶具有操作简单、透明度高等特点，是制作工艺饰品的较佳选择。传统水晶滴胶的制作原料主要为环氧树脂AB胶，是由环氧树脂和固化剂组成的双组分高分子材料，具有无毒、无污染、透明度高、硬度高、粘度低、成本低等优点[7]。随着化工业的迅速发展，新型滴胶材料UV胶进入大众视野。UV胶又称光敏胶、紫外光固化胶[8]，是一种通过紫外线照射实现快速固化的滴胶材料。本研究选用传统水晶滴胶与新型滴胶材料UV胶来制作植物工艺饰品，比较不同操作方法、不同胶体对工艺饰品制作效果的影响，探究水晶滴胶工艺饰品的制作方法，为其推广应用提供参考。
1 材料与方法
1.1 试验器材 DHG-9070A型电热恒温鼓风干燥箱，DenverTP-114型电子天平，36W紫外线灯（波长：365～405nm）。硅胶模具，一次性塑料分胶杯，滴胶搅拌棒，一次性塑料滴管，剪刀，标本夹，牙签。普通高透环氧树脂AB胶（硬胶），新型UV胶（硬胶）。试验所用植物材料均取自阿坝师范学院校园内，主要为植物花朵及彩叶。
1.2 试验方法
1.2.1 植物材料处理 选取健康、形态完整的植物材料，整形后置于标本夹中，上下两面均用报纸覆盖包裹，然后将其夹紧，置于50℃的恒温干燥箱中进行恒温加热快速干燥植物标本，更好地保存植物花叶的色泽和形态[9-11]。
1.2.2 植物花叶标本制作 分别采用传统环氧树脂AB胶与新型UV胶制作植物标本饰品，制作过程中记录气泡产生情况及固化时间，观察固化脱模后成品的颜色、透明度、硬度。
（1）环氧树脂AB胶混合与包埋脱模。配制滴胶：用天平分别称取适量A胶3份，然后按照一定质量比（A胶∶B胶=3∶1）称取适量的A、B胶，将A胶与B胶分别按表1的3种操作方法（C1、C2、C3）进行混合，记录气泡产生情况及固化时间。包埋脱模：将配制好的胶体先倒入模具一半的位置，把植物标本放入其中，并进行整形，使其美观。如有气泡产生，用针头或牙签将气泡挑出，静置直至气泡消失。然后分别将模具置于特定试验条件（C1、C2、C3）进行固化。待下层胶体基本能将标本固定住不再上浮，再立即配制第2份滴胶，然后进行模具空余部分的填充，待其完全凝固后进行脱模。
（2）新型UV胶包埋脱模。将植物标本放置在模具中进行整形，然后取少量UV胶涂抹于标本的不同部位，用紫外灯进行照射，将标本固定于模具内。标本固定后缓慢向模具中倒入1层UV胶，如有气泡，用牙签挑出，然后用紫外灯进行照射，待底层胶体凝固后再倒入1层UV胶，然后用紫外灯照射，重复上述操作直至填充完成。UV胶在紫外灯的照射下凝固较快，但在凝固过程中要注意少量多次倒胶，待底层胶体完全凝固后再倒下一层胶体，以防中间胶体未完全凝固导致后续出现凝固不了的现象。待胶体完全固化后进行脱模。 1.2.3 标本、饰品的后期制作 将固化好的滴胶产品进行打磨抛光和装饰，镶嵌上挂绳、金属扣等，制成精美成品。
2 结果与分析
2.1 不同制作方法的滴胶工艺饰品效果 由表2及图1可知，相较于常规操作方法（C1组），C2、C3组制作的滴胶（环氧树脂AB胶）工艺成品产生的气泡较少。在沸水浴中进行混合搅拌的C2组，在刚完成填充时产生的气泡较少或不产生气泡，但在后续凝固过程中会逐渐产生气泡，完全固化所需的时间较C1组短。水浴可降低树脂黏度，增加流动性[13]。而包埋后放置于恒温干燥箱（40℃）中固化的C3组产生的气泡最少，且固化时间最短。由此可见，40℃恒温条件能有效加快反应速度，缩短固化时间[12-13]。
2.2 不同材质滴胶制作的工艺饰品效果 使用新型UV胶制作植物工艺饰品步骤简单，完全固化所需的时间也大幅缩短，成品的透明度和硬度与环氧树脂AB胶制作的成品相当（表2、图2）。由于操作过程无需混合胶体，大大减小了气泡产生的可能性。环氧树脂AB胶制作的成品呈透明色，但UV胶在完全固化后成品胶体会微微泛黄，在制作颜色丰富的植物工艺饰品时会产生轻微的色差（图2）。
2.3 不同植物材料制作的工艺成品 通过对比植物彩叶（层次简单）和花朵（层次复杂）制成的滴胶（环氧树脂AB胶）饰品成品，发现花朵工艺饰品比叶类更容易产生气泡（图1、图2）。由于花瓣间具有空隙，直接倒胶会导致胶体不能完全填充进每一个缝隙，在缝隙间就极易产生气泡，后续凝固时气泡会受温度等影响上浮或是附着在花瓣上，影响成品的美观性。因此在制作花朵类滴胶时，可先用一次性的塑料滴管吸取少量胶体，填充进花瓣中，确保每一片花瓣都均匀涂抹上滴胶，待花瓣上的滴胶凝固后再将花朵进行整体包埋。这不仅可以减少气泡的产生，还可以在操作过程中给花瓣整姿，使花朵呈现出更好的美观性。
3 结论与讨论
试验结果表明：水浴加热混合水晶滴胶、恒温（40℃）条件下进行固化可有效缩短固化时间，减少气泡的产生，制作的水晶滴胶工艺饰品效果最佳;新型UV胶操作简单、气泡少、固化时间短，但对成品颜色稍有影响，对成品颜色有高精度要求的应不予考虑。同时，层次复杂的植物材料操作难度更大，影响水晶滴胶标本成品效果。相较于传统工艺饰品制作方法，环氧树脂AB胶与新型UV胶制作的标本具有透明度高、硬度高、操作简单等特点，可有效保存植物标本的颜色及立体姿态等。UV胶的使用更是精简了标本制作步骤，大幅缩短固化时间，减少气泡的产生，提高了成品制作的成功率。但UV胶的固化需要紫外线灯进行照射，紫外线照射空气时会产生臭氧，对人体会造成伤害[8]，而且UV胶是新型滴胶材料，价格偏高。环氧树脂AB胶通过沸水浴混合与恒温固化也能够大幅缩短时间，获得质量较高的成品，成本更为低廉。两者各有优缺点，可根据具体需求进行选择。总之，水晶滴胶与UV胶均能使植物标本高度保真，具有较高的观赏价值，有利于在立体教学标本、水晶滴胶工艺饰品制作等方面的应用。
参考文献
[1]刘杰克，金梓.中国饰品市场分析及竞争策略[J].市场研究，2006（05）：5-7.
[2]张甲敏，祝勇，陈军龙.人造琥珀的制作方法[J].河南科技学院学报（自然科学版），2008（02）：59-62.
[3]有保和.人工琥珀标本的简易制作[J].生物学通报，1996（01）：38.
[4]唐安科，唐发辉，赵元莙.一种透明水溶性树脂包埋生物标本的新方法[J].重庆师范大学学报（自然科学版），2008（01）：91-92.
[5]董禎.一种新型的水晶滴胶生成技术[J].北京农业，2015（28）：197.
[6]饶星，彭姚.大学生创新创业探索实践——“手底生花”创意滴胶项目探讨[J].品牌研究，2018（02）：118-120.
[7]张建逵，邢艳萍，李倩，等.环氧树脂AB胶制作叶、花类药用植物标本的研究[J].现代中药研究与实践，2015，29（04）：24-26.
[8]张南哲，朴哲，梁永日，等.紫外光（UV）照射固化光敏胶[J].延边大学学报（自然科学版），2000（01）：67-71.
[9]李婷.干花制作技术浅谈[J].科技资讯，2008（16）：213.
[10]李芬，吴文霖，祝剑峰.干燥花制作技术[J].安徽农学通报，2020，26（12）：37-38.
[11]兰霞，盛爱武，余晓华，等.玫瑰干燥花制作工艺研究[J].北方园艺，2011（17）：158-160.
[12]张启霄，姚亚丽，安硕，等.水晶滴胶制作昆虫标本[J].实验室科学，2018，21（05）：85-87.
[13]刘冬妮，张荣荣，孙思，等.高质量树脂标本的制作与应用[J].产业与科技论坛，2015，14：77-78. （责编：徐世红）