【摘 要】
：
以过硫酸铵(APS)为引发剂,乙酸乙烯酯为接枝单体,制备了红薯渣接枝乙酸乙烯酯接枝共聚物,通过IR及SEM等测试对接枝共聚物进行了表征。考察了红薯渣接枝乙酸乙烯酯聚合反应过
论文部分内容阅读
以过硫酸铵(APS)为引发剂,乙酸乙烯酯为接枝单体,制备了红薯渣接枝乙酸乙烯酯接枝共聚物,通过IR及SEM等测试对接枝共聚物进行了表征。考察了红薯渣接枝乙酸乙烯酯聚合反应过程中引发剂浓度、单体浓度、红薯渣浓度对接枝聚合反应速率的影响,关联出在低引发剂浓度下,接枝聚合反应的速率方程为:Rg∝K[M]~(0.37)[AGU]~(0.57)[APS]~(0.28)。
Ammonium persulfate grafted vinyl acetate grafted copolymer was prepared by using ammonium persulfate (APS) as initiator and vinyl acetate as grafting monomer. The graft copolymer was characterized by IR and SEM. The effects of initiator concentration, monomer concentration and sweet potato residue concentration on graft polymerization rate were investigated in the process of vinyl acetate graft with sweet potato residue. The rate equation of graft polymerization at low initiator concentration was : RgαK [M] ~ (0.37) [AGU] ~ (0.57) [APS] ~ (0.28).
其他文献
选取乙醇、甲苯、丙酮、乙醚4种溶剂对顺,反,顺-1,2,3,4-环丁烷四甲酸二酐粗品(CBDA)进行洗涤,抽滤、恒温干燥、重结晶后得到纯度较高的CBDA产品。分析讨论了洗涤次数和4种有
采用离子交换法,通过调控N,N-二甲基甲酰胺（DMF）与H2O比例,制备出了具有可见光催化活性的菱形十二面体磷酸银。利用X射线衍射仪（XRD）、扫描电镜（SEM）、傅里叶红外光谱（FT-IR）和紫外-
以高密异收缩涤纶复合丝织物、3M气溶胶和聚四氟乙烯(PTFE)微孔膜为基材,通过层压来制备防水透湿层压复合织物,并对复合织物的剥离强力等性能进行测试,探索出复合织物的最优
合成了含硫高折光紫外光固化树脂,采用红外光谱(FT-IR)、核磁和质谱表征了树脂结构。配制了一系列紫外光固化体系,用FT-IR表征了固化过程特征吸收峰的变化。测试了紫外光固化
以六水合硝酸锌和2-甲基咪唑为原料,以二甲基甲酰胺(DMF)为溶剂,以丙酮为纯化试剂,通过微波辅助加热法合成沸石咪唑酯骨架材料-8(ZIF-8),并采用XRD、BET和SEM对制得产物的结
伴随语言学理念与多媒体技术的发展,多模态教学模式在大学英语教学中的应用越来越广泛.本文从当前我国大学英语课程设置的主要观点出发,提出按需求设置课程、应用多模态的教
采用高压静电纺丝法制备热塑性聚酯弹性体(TPEE)纳米纤维膜,再通过水热法将水滑石(LDH)负载在纳米纤维表面,制备出TPEE@LDH复合纳米纤维膜,并对其进行红外光谱(FT-IR)、能谱(
以羟基封端的聚二甲基硅氧烷(PDMS-OH)与三甲氧基硼氧六环(TMOB)为主要原料,采用缩聚方法制备线性硅硼聚合物;再加入异佛尔酮二异氰酸酯(IPDI)制备新型冲击硬化材料。在通过
通过两种不同的方法对秸杆进行预处理,制备秸杆/废旧塑料复合材料,利用拉力试验机和冲击试验机对材料力学性能进行表征,利用偏光显微镜和扫描电子显微镜对复合材料进行微观分
m维列向量y和yT做乘积运算,可以获取秩为1的矩阵yyT.秩为1的矩阵自身具有一定的优势与特性.本文简要介绍预备知识,包括1个定义、3个引理,在其基础上讨论矩阵yy T的主要相关特