【摘 要】
：
In view of the higher temperature of large- size Ni/ MH battery in electric vehicle, the effect oftemperature on electrochemical performances of hydrogen storag
【机 构】
：
Teaching and Research Section of Machinery Design
论文部分内容阅读
In view of the higher temperature of large- size Ni/ MH battery in electric vehicle, the effect oftemperature on electrochemical performances of hydrogen storage alloy Ml ( NiCoMnTi )5 was investigated systematically.The results show that the electrochemical performances of alloy vary drastically with temperature changing.As temperature rises, the hydrogen equilibrium pressure increases, the width of hydrogen desorption plateau decreases and the gradient increases, leading to a decline of capacity.When temperature rises from 20 ℃ to 80 ℃, dischargeability is improved markedly.Higher temperatures also bring about a significant decrease in the cycling stability and self- discharge property.X-ray diffraction analysis indicates that the alloy has a single phase withCaCu5-type LaNi5 structure.
其他文献
The room-temperature oxygen plasma treatment before depositing ZnO films on nanocrystalline diamond substrates was studied. The nanocrystalline diamond substrat
The effect of Nb in (La0.5Ce0.5)64-xAl16Ni5Cu15Nbx (x=0-5, mole fraction) bulk metallic glasses was investigated by X-ray diffractometry, differential scanning
In order to evaluate the effect of stoichiometric ratio upon electrochemical properties of AB5-type hydrogen storage alloys, a series of alloys Mm0.8La0.2(Ni4.0
The deformation behavior of squeeze cast ZK60 magnesium alloy was investigated by compressive tests conducted at temperatures of 250-450 ℃ and strain rates of
The effects of reactive gas partial pressure on droplet formation,deposition rate and change of preferred orientation of CrN and Cr2O3 coatings were studied. Fo
Many factors were found to have effects on the conversion coatings for AZ31 alloy, alloy the most important one in producing high quality conversion coatings is
The 7××× aluminum alloys having a microstructure with precipitate free zones (PFZ) nearby the grain boundary, have received a great deal of attention due to
The photoconductive characteristic of the inorganic/organic hybridized polymer system is reported,in which a novel bi-functional photorefractive (PR) poly(N-vin
Intermetallic compounds(IMC) formed at Sn-Ag-Cu solder droplet/pad interface during wetting reaction were investigated.Comparative studies of the IMC evolution
Al-Zn-Mg-Cu-Zr ingots with diameter of 200 mm were made by low frequency electromagnetic casting (LFEC) and conventional direct chill (DC) casting process. The