【摘 要】
：
在聚乙烯吡咯烷酮(PVP)存在下,以无水Na2CO3为控制剂,利用微波辅助多元醇法快速加热还原硝酸银制备了球形Ag纳米颗粒,研究了Na2CO3的添加量对球形Ag纳米颗粒大小的影响。用扫
【机 构】
：
太原理工大学新材料界面科学与工程教育部重点实验室,
论文部分内容阅读
在聚乙烯吡咯烷酮(PVP)存在下,以无水Na2CO3为控制剂,利用微波辅助多元醇法快速加热还原硝酸银制备了球形Ag纳米颗粒,研究了Na2CO3的添加量对球形Ag纳米颗粒大小的影响。用扫描电镜(SEM)、透射电镜(TEM)、X射线光电子能谱(XPS)、X射线衍射(XRD)和紫外-可见吸收光谱(UV-Vis)对制备的银纳米颗粒的形貌、组分、粒径和相结构进行了表征。结果表明,制备的Ag纳米颗粒的平均粒径随着Na2CO3添加量的增大而逐渐减小。
In the presence of polyvinylpyrrolidone (PVP), spherical Ag NPs were prepared by the rapid heating reduction of silver nitrate by microwave assisted polyols method with anhydrous Na2CO3 as the control agent. The effects of Na2CO3 addition on the size of spherical Ag NPs were studied . The morphologies of the prepared silver nanoparticles were characterized by SEM, TEM, XPS, XRD and UV-Vis. Min, particle size and phase structure were characterized. The results show that the average particle size of the prepared Ag nanoparticles gradually decreases with the addition of Na2CO3.
其他文献
Graphitic carbon nitride (g-C3N4) was synthesized by heating melamine and was then treated with sodium hydroxide solution under a hydrothermal condition to obta
作者采用苍术注射液治疗窦性心动过速(由心电图证实,心率为120—130次/分,无其他心电图异常改变)共19例,其剂量为每次4毫升,每日二次肌肉注射,一般用药3～5天即恢复正常者18例
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
从1975年8月～1978年1月,我们使用无创性生理方法,对323例未见明确心血管疾病之正常人和226例明确诊断心血管疾病患者,进行了心肌收缩力测定并进行了统计学处理,发现心力系数
用原位自生技术制备了TiB增强的近α相钛基复合材料,利用金相显微镜、高温材料试验机和透射电镜(TEM)研究了热加工过程中此复合材料的魏氏组织演变和TiB晶须的取向变化,并测
近来认为急性缺血时的细胞内酸中毒能使心肌作功减退,从属于 pH 的钙-收缩蛋白相互作用的减低是造成缺血心肌作功减退的主要原因。本文报道用指示剂稀释法测量麻醉狗心肌细
针对一类控制增益未知的不确定非线性系统的输出跟踪控制问题,提出了一种自适应神经网络动态面控制器设计方案.通过采用基于状态参考的反推控制策略,放松了对用于设计期望虚
Biomedical metal materials such as titanium,magnesium and their alloys have been widely studied as orthopedic implants or cardiovascular stents due to their des
小麦抗叶锈基因Lr19来源于长穗偃麦草,表现优良的抗叶锈性,国内外发现对Lr19有毒性的小麦叶锈菌菌株的报道较少。本研究以TcLr19和Thatcher亲本以及TcLr19×ThatcherF2代单株
随着技术的发展，技术与人之间的关系已经发生了彻底的改变。从表面看来，技术给我们的生活带来了高效、便利与进步。但实际上，技术早已在不经意中替代了人类的主体性地位，从一个人