Effect of Prior Cold Deformation on the Stability of Retained Austenite in GCr15 Bearing Steel

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:pqx98
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
In this work,the effect of prior cold deformation on the stability of retained austenite in GCr15 bearing steel was investigated after quenching and tempering treatment.The thermal stability was evaluated by calculating thermal activation energy for decomposition of retained austenite using differential scanning calorimeter.The mechanical stability was investigated according to the strain-induced martensitic transformation behavior of retained austenite under the standard compression testing.It is found that the prior cold deformation not only accelerates the carbide dissolution during the austenitization process but also contributes to the carbon partitioning in the tempering stage due to the higher density of phase boundaries,which results in the improvement of the thermal stability of retained austenite.Due to the enhanced carbide dissolution,the higher carbon content in the prior austenite will intensify the isotropic strain of martensitic transformation.As a consequence,the film-like retained austenite is likely to form under a higher hydrostatic pressure and thus shows a higher mechanical stability.Additionally,it is noteworthy that the benefits of the prior cold deformation to the stability of retained austenite would be saturated when the cold deformation degree is larger than 40%.
其他文献
To explore the optimum use of stabilised elements and study the influences of stabilisation in 18Cr-2Mo grades,the Nb and Nb + Ti microalloying investigation focused on the relationships of the microstructure and mechanical properties of the microalloyed
Rutile (TiO2) particle-reinforced aluminum matrix composites were prepared by friction stir processing.The microstructure was studied using conventional and advanced characterization techniques.TiO2 particles were found to be dispersed uniformly in the co
In this research,2205/Q235B clad plates were prepared by a vacuum hot rolling composite process.The effects of adding Fe,Ni,and Nb interlayers on the bonding interface structures and the shear strengths of the clad steel plates were studied.The results sh
Coarsening of cuboidal γ\'precipitates and relevant diffusion process in Ni-based single-crystal superalloy CMSX-4 were investigated at 1000,1020 and 1040 ℃ for specific times.The γ\'coarsening kinetics followed a cubic rate law with time and was pres
The microstructure and mechanical properties of NiCrMoV-and NiCrSi-alloyed medium-carbon steels were investigated after multiple tempering.After austenitising,the steels were hardened by oil quenching and subsequently double or triple tempered at temperat
To understand the atomistic mechanisms of tension failure of Ni-based superalloy,in this study,the classical molecular dynamics (MD) simulations were used to study the uniaxial tension processes of both the Ni/Ni3Al interface systems and the pure Ni and N
In the present work,the electrochemical behavior and properties of the passive film of a new Sn-alloyed 316LX austenitic stainless steel were investigated.With the increase in Sn content in 316LX austenitic stainless steel from 0 to 0.21%,the critical pit
Mg-2Al-1.2Ca-0.2Mn (at%)-based alloys with Ce-rich mischmetal (MM) substitution of 0-0.6 at% for Ca were hot extruded at 400 ℃.The effect of MM substitution on the microstructure and mechanical properties of the extruded alloys was investigated.The as-cas
The high-current pulsed electron beam (HCPEB) treatment with current density 6 J/cm2 was applied on AZ91 Mg alloy to improve its corrosion resistance.Results showed that the net-like Mg17Al12 disappeared on the surface of AZ91 Mg alloy after irradiation b
The effect of lead on the initial corrosion behavior of 316LN stainless steel has been investigated by U-bend immersion experiments in 4 wt% NaOH solutions at 300 ℃.Follow-up studies after soaking were carried out by scanning electron microscope,energy di