【摘 要】
：
本文叙述了夹杂物变性的涵义,举例说明了经变性处理后的球状夹杂物,可以收到改善钢的各项性能的效果,分析了电炉——VHD——钢包 CaSi 处理工艺条件下,球状夹杂物的组成和结
论文部分内容阅读
本文叙述了夹杂物变性的涵义,举例说明了经变性处理后的球状夹杂物,可以收到改善钢的各项性能的效果,分析了电炉——VHD——钢包 CaSi 处理工艺条件下,球状夹杂物的组成和结构,指出了钢中固溶钙量,与球状夹杂物结构式的关系;探讨了球状夹杂物形成机理,提出了促进钢中夹杂物变性球化的新工艺。
This paper describes the meaning of inclusions denaturation, an example of the denatured spherical inclusions can receive the effect of improving the performance of the steel, the electric furnace - VHD - ladle CaSi processing conditions, spherical inclusions The composition and structure of the steel were discussed. The relationship between the amount of dissolved calcium in steel and the structure of spherical inclusions was pointed out. The formation mechanism of spherical inclusions was discussed. A new process was proposed to promote the transformation of inclusions in steel.
其他文献
测定了610型镇静钢锭帽口凝固过程的温度场分布及变化,计算并编制了热平衡图,找出三种不同保温材质对钢锭帽口热效率的影响。热工测定和计算表明:现有生产条件下,本钢一钢厂
钕铁硼磁体是继钐钴磁体后又一重要的稀土磁体。由于它具有原料来源丰富,价格便宜,磁性能好等特点,可使磁铁产品小型化,高性能及高精度化等以适应追求产品轻、薄、短、小的
随着炼铁技术的发展,高炉生产率不断提高,但是由于各种原因,高炉生产过程中出现的各种操作事故仍未完全消除,高炉结瘤就是其中一例。在某些炼铁厂中高炉结瘤成为提高生产水
近年来,对钢丝绳的需求量越来越大,刺激了钢丝绳生产企业采取措施,扩大生产能力,改造或引进设备,同时钢丝绳进口量也在逐年增加。在这种形势下,分析近年来钢丝绳的产需现状
日本专利昭56—108813号介绍了一种用高炉渣对铁水进行预处理的方法。所用高炉渣的成分为:CaO25～50％,SiO_220～45％,Al_2O_310～20％,P_2O_5
本文提出了一种综合利用含铜镁砖的新方法。此法包括粉碎、筛选和浮选等过程。为了成功地实现铜的浮选,用黄药和黑药作捕收剂,硫化钠作活化剂。用此法可生产出含铜约40％的精矿
选择碳素铬铁熔炼炉渣成分的原则,最初是由 A.M.萨马林研究拟定的。他提出用∑RO·SiO_2+R_2O_3渣型的酸性渣冶炼。后来,对用不同产地的铬矿熔炼碳素铬铁时的终渣(废渣)成分
铝工业用拜耳法生产氧化铝,产出具有一定价值的铝土矿残渣(赤泥和砂)。表1中列出了这种残渣中元素含量的大致范围。各种元素按含量多寡排列。这类残渣的可能用途之一是制砖
炉前冲渣是渣处理工艺的一项重要改革。根据鞍钢炼铁厂一排高炉的地理位置、外运条件及能耗重要指标的相对比较,选用渣池法的冲渣工艺最为适合。渣池法具有投资少、生产可靠
本文概括了我国烧结厂使用生石灰的情况及效果。并重点介绍了马钢一烧和苏联扎波罗什烧结厂生产生石灰的方法。文中提出了一个煅烧生石灰的改造方案,有待于生产验证。
This