The as-cast Cu-doped Fe83Ga17 alloys were prepared by arc-melting.The microstructures and magne-tostrictions of(Fe83Ga17)100-xCux(x=0,3,6,9,12,15)alloys were in
【机 构】
:
Inner Mongolia Key Laboratory for Physics and Chemistry of Functional Materials,School of Water Cons
【基金项目】
:
the National Natural Science Foundation of China(No.51661027),the Natural Science Foundation of Inner Mongolia(No.2019MS05002)。
论文部分内容阅读
The as-cast Cu-doped Fe83Ga17 alloys were prepared by arc-melting.The microstructures and magne-tostrictions of(Fe83Ga17)100-xCux(x=0,3,6,9,12,15)alloys were investigated by X-ray diffraction,scanning electron microscopy,energy dispersive spectroscopy and strain gauge magnetostriction measurement.Vibrating sample magnetometer was employed to investigate the magnetic properties of(Fe83Ga17)100-xCux(x=0,3,6,9,12,15).First-principal calculation was employed to make lattice structure and energy simulation.The results indicate that Cu dopants dissolve into A2 lattice by interstitial doping,which induces tetragonal-like distortion of A2 lattice.And the magnetostriction for Cu-doped Fe83Ga17 alloys is lower than that of Fe83Ga17 alloy.The reduction of magnetostriction is attribute to the increase of Young\'s modulus caused by Cu dopants dissolve into A2 lattice by interstitial doping and the decrease of magnetoelastic coupling coefficient for Cu-doped Fe83Ga17 alloys caused by Cu dopants dissolve into A2 lattice.
其他文献
Microstructures and tensile properties of a newβhigh-strength titanium alloy Ti-5321(Ti-5 Al-3 Mo-3 V-2 Zr-2 Cr-1 Nb-1 Fe)were investigated in this study.Four microstructures,including equiaxed microstructure(EM),bimodal microstructure(BM),basket-weave mi
A short process of Inconel 625 alloy tube was developed to solve the problems of the traditional extrusion process,and particular attention was paid on the hot deformation behavior of the as-cast Inconel 625 alloy.The hot compression experiments were perf
It is important to understand the correlation between grain morphology and intervariant boundaries of theαphase after heat treatment belowβtransus of the electron beam melted(EBMed)Ti-6 Al-4 V alloy.Scanning electron microscopy(SEM)and electron backscatte
The controlled preparation of hexagonal tung-sten trioxide(h-WO3)nanostructures was achieved by adjusting the pH of the precursor solution.The effect of the pH
Microstructures and mechanical properties of Mg-4.5 Y-2.5 Nd-1.0 Gd-0.5 Zr-xZn(x=0,0.5,1.0,and 1.5;wt%)alloys under as-cast and peak-aged states were investigated in this work.The results indicate that the intermetallic phase components are closely depend
Rejuvenation heat treatments can restore the microstructures and mechanical properties of the degraded turbine blades in gas turbine engines.Herein we analyze the effects of rejuvenation heat treatments on the microstructural characteristics and mechanica
Cerium dioxide has a comparatively lower Ce4+/Ce3+redox pair,which leaves abundant oxygen vacancies on oxide lattice,also making incorporation of foreign ion and subsequent applications feasible and convenient.In this work,a series of cerium-yttrium mixed
Hot-rolled high-Mg-alloyed Al-Mg alloy(Al-9.2 Mg-0.8 Mn-0.2 Zr-0.15 Ti,labeled as 5 A12)plates were successfully friction stir welded at rotating rates ranging from 750 to 1500 r·min-1 at a constant welding speed of50 mm·min-1.The jo
The successful joining of carbon fiber-reinforced aluminum matrix(Cf/Al)composites and TC4 alloy can produce composite structure and meet the demands of lightwe