Effective improvement in electrical properties of NO passivated SiC/SiO2 interface after being irradiated by electrons is demonstrated.The density of interface traps after being irradiated by 100-kGy electrons decreases by about one order of magnitude,specifically,from 3 × 1012 cm-2.eV-1 to 4× 1011 cm-2.eV-1 at 0.2 eV below the conduction band of 4H-SiC without any degradation of electric breakdown field.Particularly,the results of x-ray photoelectron spectroscopy measurement show that the C-N bonds are generated near the interface after electron irradiation,indicating that the carbonrelated defects are further reduced.