Structural strengthening of the nano porous silica films has been reported. The films were prepared with a base/acid two-step catalyzed TEOS-based sol-gel processing and dip-coating, and then baked in the mixed gas of ammonia and water vapor. The silica films were characterized with TEM, AFM, FTIR, spectrophotometer, ellipsometer, and abrasion test, respectively. The experimental results have shown that the films have a nanostructure with a low refractive index and can form an excellent scratch-resistant broadband anti-reflectance. The two-step catalysis noticeably strengthens the films, and the mixed gas treatment further improves mechanical strength of the silica network. Finally the strengthening mechanism has been discussed.
Structural strengthening of the nano porous silica films has been reported. The films were prepared with a base / acid two-step catalysed TEOS-based sol-gel processing and dip-coating, and then baked in the mixed gas of ammonia and water vapor. The silica films were characterized with TEM, AFM, FTIR, spectrophotometer, ellipsometer, and abrasion test, respectively. The experimental results have shown that the films have a nanostructure with a low refractive index and can form an excellent scratch-resistant broadband anti-reflectance . The two-step catalysis noticeably strengthens the films, and the mixed gas treatment further improves mechanical strength of the silica network. Finally the strengthening mechanism has been discussed.