【摘 要】
：
The microstructure and properties of the 93W-4Ni-2Co-1Fe (mass fraction, %) tungsten heavy alloys prepared by mechanical alloying and electric current activated
【机 构】
：
National Metallic Materials Net-shape Forming Engineering Research Center
论文部分内容阅读
The microstructure and properties of the 93W-4Ni-2Co-1Fe (mass fraction, %) tungsten heavy alloys prepared by mechanical alloying and electric current activated sintering from mixed elemental powders were investigated. After 15 h milling, the average W grain size in the powders is decreased to 120 nm. For the powders milled for 15 h, the density, hardness and transverse rupture strength of the alloys sintered only by an intensive pulse electric current are the maximum. When the total sintering time keeps constant, the properties of the sintered alloys can be obviously improved by optimizing the sintering time of pulse- and constant-currents. A bulk ultrafine alloy with an average W grain size of about 340 nm can be obtained by sintering 15 h-milled powders in a total sintering time of 6 min. The corresponding sintered density, hardness and transverse rupture strength reach 16.78 g /cm3, HRA84.3 and 968 MPa, respectively.
其他文献
The accuracy of nucleation parameter is a critical factor in the simulation of microstructural evolution during dynamic recrystallization (DRX). Based on the fl
The Ti-35%Nb (mass fraction) foams were prepared by a powder metallurgy method, and the microstructure and the mechanical properties of the foams under monotoni
Extensive testing was carried out to study the effects of rare earth Ce doping on the properties of SnAgCu solder alloys. The addition of 0.03% (mass fraction)
It is economically advantageous to cast wrought aluminum alloys directly into near-net-shape components. The objective of the present work is to take advantage
The influence of the manganese-alloying on the structure and magnetocaloric properties of the Gd5Si2.05Ge1.95 compound was studied by X-ray powder diffraction a
Ce-doped ZnO films were prepared by the sol-gel method with spin coating onto glass substrates.Zinc acetate dihydrate,ethanol,diethanolamine and cerium nitrate
The cross-sectional distortion usually appears during rotary-draw bending process of thin-walled rectangular tube with small bending radius. To study the cross-
Ce-Cu-O monolithic catalysts were prepared by using Ce0.9Cu0.101.9 solid solution or nitrate as precursors,and their catalytic performance for the combustion of
Using solid-state synthesis method,a series of samples of lanthanum doped Li1-xLaxFePO4(x=0.0025,0.005,0.0075,0.01)were prepared.Each cathode structural and ele
In order to obtain the thermodynamic description of the Mg-Ga binary system, the thermodynamic assessment of the system was carried out using the CALPHAD method