Compression tests at room and high temperature and creep tests at high temperature have been performed on B2 Nb15A120V and Nb10A120V alloys. At room temperature
The multiple scattering cluster (MSC) method has been employed to perform a theo-retical analysis on carbon 1s near edge X-ray absorption fine structure of the
The Mg-Al-Zn series AZ31 and AZ314+MM alloys are homogenized at 673, 723 and753K respectively. The hardness of alloy ingots at different heat-treated states ism
The structural evolution of undereooled single-phase Ni-2wt%Pb monotectic alloy wassystematically investigated by using the method of molten glass denucleating