The sulfide stress corrosion cracking( SSC) performance of G3 and 028 nickel-based alloys w as studied using slow strain rate test( SSRT) and the four-point bend( FPB) test under simulated dow nhole conditions. The effect of high temperature,high H2 S / CO2 partial pressure,and the presence of sulfur on SSC susceptibility w as investigated. The G3 alloy w as found to have a higher SSC resistance than the 028 alloy. Presence of sulfur and temperature bear a strong influence on the SSC performance of the metals,particularly on the 028 alloy. The applicability of 028 and G3 alloys may be expanded and both could safely be used beyond the limits set by the ISO15156-3 standard.
The sulfide stress corrosion cracking (SSC) performance of G3 and 028 nickel-based alloys w as studied using slow strain rate test (SSRT) and the four-point bend (FPB) test under simulated dow nhole conditions. The effect of high temperature, High H2 S / CO2 partial pressure, and the presence of sulfur on SSC susceptibility w as investigated. The G3 alloy w as found to have a higher SSC resistance than the 028 alloy. Presence of sulfur and temperature bear a strong influence on the SSC performance of the metals, particularly on the 028 alloy. The applicability of 028 and G3 alloys may be expanded and both could safely be used beyond the limits set by the ISO15156-3 standard.