采用传统摩擦焊焊接方法连接具有良好非晶形成能力的Zr65Cu12.5Al7.5Ni15(at%)块体非晶合金。微区X射线衍射结果显示,整个焊接接头保持了非晶特性,无晶化反应发生。对摩擦焊焊接方法成功连接块体非晶合金Zr65Cu12.5Al7.5Ni15的原因进行了分析。
A conventional amorphous alloy of Zr65Cu12.5Al7.5Ni15 (at%) with good amorphous formability was joined by the traditional friction welding method. X-ray diffraction results show that the entire welded joints to maintain the amorphous nature of non-crystallization reaction. The reason why the bulk amorphous alloy Zr65Cu12.5Al7.5Ni15 was successfully connected by friction welding method was analyzed.