其他文献
为了明确Mo、Ce、Ti在贝氏体钢中的作用,采用热力学计算结合试验,研究含钛贝氏体钢中Mo和Ce对钢中第二相析出、组织转变及性能的影响机制。结果表明,贝氏体钢中加入Mo后,部分固溶于钢基体中,部分以碳化钼的形式析出,Ti以C2S2Ti4析出为主,Ce在钢中以Ce2O3和Ce2O2S的形式存在,加Ce后Ti的第二相析出以TiC为主;Mo的加入使Ti(C,N
The growth of Arthrospira platensis and physiological changes in biomass under the effects of six rare earth elements Dy, Sm, Tb, La, Nd and Yb were evaluated.
针对低热值燃气燃烧温度低导致烧结点火质量差的问题,采用描述碳氢火焰燃烧的化学动力学详细机理GRI-Mech3.0对低热值燃气的燃烧过程进行模拟;研究了富氧条件对低热值燃气燃烧温度、烟气氧浓度和燃烧速率的影响;开展了低热值燃气富氧点火技术的工业化试验。研究结果表明,采用富氧空气作为助燃剂可以显著提高低热值燃气点火温度,改善点火效果;当助燃风氧体积分数提高至0.23时,纯高炉煤气点火效果可以提高至与采用空气加混合煤气的点火效果相等;进一步提高助燃风氧含量使得烧结点火能耗相应降低,表层烧结矿质量相应增加。工业化
高温合金铸锭凝固过程内部各区域散热条件不同,冷却速率存在明显差异。采用差示扫描量热分析(DSC)、高温共聚焦显微镜(HT-CLSM)原位观察和定向凝固(DS)的方法,研究了宽冷速范围下GH4738合金的凝固偏析和碳化物析出行为。结果表明,GH4738合金的凝固顺序为L→γ+L,L→γ+L+MC,L→γ+MC+η+(γ+γ′),其中MC型碳化物、η相和(γ+γ′)共晶相为合金凝固过程中的主要偏析产物;Ti、Mo元素是合金的主要枝晶间偏析元素;提高冷却速率能有效降低凝固前沿残余液相中的溶质富集程度;铸态组织中
Benefit from the enhanced onboard processing capacities and high-speed satellite-terrestrial links,satellite edge computing has been regarded as a promising technique to facilitate the execution of the computation-intensive applications for satellite comm
详细研究了奥氏体化温度对中碳调质钢40CrNiMo的淬透性、以0.7℃/s淬火后组织及调质处理后组织和性能的影响。研究结果显示,随着奥氏体化温度从800提高至1 000℃,材料的淬透性逐渐增加,尤其是当奥氏体化温度提高至950℃以后,淬透性增加幅度显著变大。当奥氏体化温度为800℃时,组织中存在相对多的铁素体,使得淬火后材料的硬度较低,但回火后具有最佳的韧性;奥氏体化温度为900℃时,高温回火后试样具有最高的强度,但塑性较低。随着奥氏体化温度的升高,材料的断裂机制发生明显变化,拉伸断裂均为典型韧性断裂,断
Binary nanocrystalline rare-earth hexaboride is regarded as one of the promising optical absorption materials that possess the high transparency for visible light and the strong absorption for NIR due to the effects of localized surface plasmon resonance.
针对集团用户市场业务的发展,采用DTMB技术,实现了集团用户高清数字电视的传输。提出基于动态负载均衡的数字电视系统优化算法,从连接方式、恢复模式、性能分配等3个方面,克服了集团用户业务中断、流量不均、恢复时间长等的缺点。
铅作为高炉原料中的一种微量元素,在高炉内循环富集会对高炉冶炼产生一系列不利影响。为了明确PbO对原燃料冶金性能的影响,通过气相吸附法制备不同铅含量的烧结矿、球团矿和焦炭样品,采用扫描电子显微镜对反应前后的富铅样品进行微观分析,研究富铅后原燃料冶金性能的变化。结果表明,铅以PbO的形式吸附在烧结矿、球团矿和焦炭的表面和孔隙中;PbO对烧结矿和球团矿还原以及焦炭的气化反应起到一定的催化作用,当表面吸附的铅含量较高时,会降低其催化作用,但对焦炭反应后强度影响不大。
在护炉阶段,炉缸活性受到一定的影响,活跃炉缸是高炉生产操作的核心工作。分析了影响炉缸活性的主要因素,并通过稳定焦炭质量、上下部调剂获得合适的两道气流,保持充沛的炉温和合适的渣碱度,优化出铁组织,保持合适的钛负荷等技术措施活跃炉缸,使得炉缸工作状况好转,炉缸炭砖温度高点逐步下降至可控范围,经济技术指标得以适当恢复,实现了炉役后期高炉的安全生产和技术指标的回升。