利用Gleeble-3008热模拟机研究了S32654超级奥氏体不锈钢在950~1 250℃、应变速率为0.001~10 s~(-1)条件下的热压缩变形行为,并建......
Constitutive Modeling for Flow Behaviors of Superaustenitic Stainless Steel S32654 during Hot Deform
Hot deformation behavior of superaustenitic stainless steel S32654 was investigated with hot compression tests at temper......