TiB2-B4C相关论文
High-pressure Sintering of Boron Carbide-Titanium Diboride Composites and 1ts Densification Mechanis
A high-pressure hot-pressing process was applied to densify a commercial boron carbide-titanium diboride (B4C-TiB2) powd......
在5.0 GPa及1500~2000℃的压力和温度条件下,采用高压烧结的方法制备了B4C含量分别为10%和30%的TiB2-B4C陶瓷复合材料。对TiB2-B4C......