WC-10Co相关论文
为明确硬质合金微观组织及力学性能最佳的配碳区间,配制了不同碳含量的WC-10Co复合粉末,并通过压制、烧结获得硬质合金.采用金相显......
The nanocrystalline WC-10Co composite powders were produced with the processing method of spray thermal decomposition-co......
采用钨、碳和钴粉为原料,直接混合后经短时间高能球磨再通过碳化反应制备出纳米WC-10Co(质量分数)复合粉;分别用XRD和SEM分析了球......
通过球磨与低压烧结方法,制备了超细晶WC-10Co合金。采用X射线衍射、扫描电镜和断裂韧性测试,研究了LaB6掺杂对超细晶WC-10Co合金......
A solid state synthesis of ultrafine/nanocrystalline WC-10Co composite powders was reported from WO3, Co3O4 and carb......
Influences of Carbon Content on the Properties and Microstructure of Ultrafine WC-10Co Cemented Carb
WC-10Co nanocrystalline composite powders prepared by spray pyrogenation-continuous reduction and carburization technolo......
Atomic force microscope study of WC-10Co cemented carbide sintered from nanocrystalline composite po
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生......
ultrafine/nanocrystalline WC-10Co 合成粉末的稳固的州的合成从 WO 被报导<潜水艇class=“ a-plus-plus ”> 3 </sub>,公司<潜......
采用热压烧结方法在温度1380℃、保温60min、烧结压力30 MPa条件下制备了立方氮化硼（CBN）颗粒体积分数为30％的WC-10Co超细硬质合金复......
本文以液相复合-连续还原碳化方法制备的掺杂有VC和Cr3C2抑制剂的纳米复合WC-10Co粉末为原料，采用真空烧结＋低压处理的工艺制备超细W......
The effect of addition of metallic carbides Cr3C2 and Cr3C2 + VC on structure and mechanical properties of WC-10 wt% Co ......
回 回 产卜爹仇贱回——回 日E回。”。回祖 一回“。回干 肉果幻中 N_。NH lP7-ewwe--一”＄ MN。W;- __._——————》 砧叫]们......
研究了WC-10Co超细晶硬质合金注射成形过程的各种影响因素,优化了球磨、注射、脱脂和烧结工艺。结果表明:在1 440℃下真空烧结1.0h......
通过向WC-10Co混合粉末中加入2%和4%质量分数的η相粉末和等摩尔量的炭黑,经过传统的粉末冶金工艺制备含板状WC晶粒的硬质合金,研......
在复合添加VC／Cr3C2的基础上，添加不同配比的TaC和Y2O3作为WC晶粒长大抑制剂，研究了晶粒长大抑制剂不同组合、含量对WC-10wt％Co超细硬......