【摘 要】
：
To improve the temperature stability of PMN(Pb(Mg1/3Nb2/3)O3)-based ceramics, PMN-based composite ceramics were prepared by co-sintering method of two kinds of ceramics with different curie temperatur
【机 构】
：
The College of Science, Air Force Engineering University, Xi’an, 710051, China
论文部分内容阅读
To improve the temperature stability of PMN(Pb(Mg1/3Nb2/3)O3)-based ceramics, PMN-based composite ceramics were prepared by co-sintering method of two kinds of ceramics with different curie temperature. One unit is MHT(0.82PMN (Pb(Mg1/3Nb2/3)O3)-0.18PT(PbTiO3)(the curie temperature Tm=74°C)), and the other unit is MLT(0.88PMN(Pb(Mg1/3Nb2/3)O3)-0.12BT(BaTiO3)(the curie temperature Tm=-50°C)). The effects of sintering temperature and the ratio of high and low Tm units on dielectric temperature stability were studied. The results show that the temperature stability can be improved greatly by co-sintering and coating method and PMN(Pb(Mg1/3Nb2/3)O3)-based composite ceramics are promising candidate for practical applications.
其他文献
本文采用微波CVD法制备了磷酸铁锂/气相生长炭纤维（VGCFs）复合正极材料。借助X射线衍射仪、场发射扫描电子显微镜和电化学测试仪研究了不同温度下制备材料的结构和电化学性能。结果表明，当温度低于600℃时，由于VGCFs导电网络的逐渐形成，材料的放电比容量随着温度的提高而增加；但当温度进一步升高时，由于磷酸铁锂的晶粒异常长大，锂离子的扩散距离增加，反而导致材料的放电比容量降低。研究发现，当温度为6
采用恒温浸泡，交流阻抗和极化曲线的方法分别研究了铸态(F)和固溶态(T4)的NZ30K以及挤压态 AZ31镁合金在浓度分别为1 mol/L，1.5 mol/L，2 mol/L的MgCl2，MgSO4，Mg(COOCH3)2，MgBr2溶液中的腐蚀行为和电化学性能。结果表明：随着电解液中电解质浓度的增加，三种镁合金自腐蚀速率均增大。F态和T4态的NZ30K合金在MgSO4溶液中腐蚀速率最快，在MgB
Spherical LiFePO4/C composite was prepared via a low-temperature solvothermal reaction followed by high-temperature treatment. The as-prepared sample was characterized by XRD, SEM, FTIR, cyclic voltam
以酚醛树脂为碳源，碱性化合物为活化剂制备了超级电容电池用炭负极材料。通过SEM和振实密度表征了材料的物化性能。应用恒流充放电法、循环伏安法及交流阻抗法考察了该炭负极材料的电池性能和电容性能。结果表明：试验制得的炭材料在1 M LiPF6/EC+DMC有机电解液中及0.2C电流密度下电池首次循环效率达55.4％，首次可逆容量为415.9mAh/g，十次循环后容量保持率为86.7%；之后增大充放电电流
通过调节前驱体FeCl3溶液的pH值，利用水热合成的方法制备出尺寸连续可调的单晶多孔α。Fe2O3颗粒。综合运用X射线衍射、扫描电子显微术、高分辨电子显微术和N2吸附对单晶多孔α。Fe2O3颗粒的形貌、尺寸、BET比表面积以及微观结构进行了研究。单晶多孔α。Fe2O3颗粒的尺寸可以从925.6±98.2nm调节到43.4±5.8nm，BET比表面积从3.97m2g-1增加到26.04m2g-1。不
采用溶胶-凝胶(Sol-Gel)法并结合旋转涂布(Dip-Coating)技术在不锈钢和单晶硅基片上沉积NiO薄膜，采用TG-DSC、XRD、SEM、循环伏安和充放电技术对干凝胶的热分解行为以及薄膜的结构、形貌和电化学性能进行表征。结果表明：以醋酸镍、柠檬酸和乙二醇为原料在一定温度下合成了性能稳定的溶胶，烧结过程中凝胶在430℃基本分解完全并逐渐形成NiO纳米晶；随着烧结温度升高，纳米NiO的结构
LiMnO2是有可能替代LiCoO2的锂电池正极材料，其电化学性能受其形貌影响，制备纳米尺寸的LiMnO2仍是一项挑战，本文使用二氧化锰、醋酸锰和氢氧化锂为原材料，采用水热合成的方法，在比较宽松的实验条件下成功制备小尺寸、底层错的单相正交LiMnO2纳米晶。X射线衍射谱强度高、带宽窄，表明材料结晶质量很好。高分辨电子显微镜图像显示沿着正交LiMnO2的b轴方向，MnO6和LiO6八面体交替排列规则
以间苯二酚（R）、甲醛（F）为原料，盐酸作催化剂，通过添加嵌段共聚物F127作制孔剂，利用溶液协同自组装和炭化处理制备多孔炭材料。采用扫描电镜和N2吸附分析不同F127加入量制得的多孔炭材料的形貌和孔隙结构，并利用直流充放电法、交流阻抗法和循环伏安法测定以上述多孔炭材料为电极的双电层电容器(EDLC)的电化学性能。结果表明：酸催化下的酚醛树脂基体网络结构在炭化过程中较好地保留了F127形成的微相结
采用扣式电池循环伏安测试（CV）、充放电测试和扫描电子显微镜（SEM）研究了工业纯镁（99.95％）、AZ31合金和Mg-1％Nd二元合金作为镁二次电池负极材料时的电化学性能和镁在电极表面的沉积形貌。结果表明：与工业纯镁相比，AZ31合金和Mg-1％Nd二元合金的溶解-沉积过电位稍高，初时循环过程的库仑效率略低，但其长期循环稳定性明显高于纯镁负极。纯镁负极在循环200次后出现了短路现象，其表面出现
以毛竹为炭前驱体，KOH作活化剂，通过调节KOH用量在相同活化条件下制备了具有不同孔隙结构的竹基活性炭材料，通过SEM、BETN2吸附、直流充放电、交流阻抗和循环伏安等结构与电化学性能分析方法，考察了碱炭比对竹基活性炭材料结构和性能的影响。研究结果表明：随着碱炭比增大，活性炭材料的比表面积与总孔容、中孔孔容、微孔孔容、微孔比表面积先增大后减小，平均孔径不断增大。其中碱炭比为6时的样品BAC6比表面