Preparation and Properties of Triazine Dithiol-Silane Composite Self-assembled hydrophobility Films

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户：meimei5211314

【摘要】

：

Self-assembled method for controllable fabrication of a hydrophobic triazine dithiol-silane composite film on 304 stainless steel (SS) is reported in this paper.Hierarchical structure composed of micr

【作者】

：

Ming-ming Hu Dong-ming Zhang

【机构】

：

State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University

【出处】

：

2014中国功能材料科技与产业高层论坛

【发表日期】

：

2014年2期

【关键词】

：

Self-assemble Hydrophobic Corrosion 304 Stainless Steel

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

DispersityonBarium-strontium Titanate Nanopowders by Microwave-hydrothermal Processing

Through the microwave-hydrothermal processing at 70℃ in 10 min, barium strontium titanate (BST) nanopowders are prepared by using butyl-titanate, barium nitrate and strontium nitrate as raw materials.

会议

barium strontium titanatedispersityOP-10polyethylene glycol 6000

Microstructure and properties of thermal sprayed ZrO2-NiCr coatings

NiCr/ZrO2 gradated coatings were obtainedon C45 carbon steel by high velocity arc spraying and micro-plasma spraying to improve the mechanical and thermalbehaviors of the carbon steel.

会议

Thermal SprayingMicrostructureHigh Temperature OxiditionThermal shock

Effect of the modification by Y, La and Chitosan for SO42-/ZrO2-TiO2-SiO2-Al2O3 type solid super aci

利用溶胶凝胶法制备SO24-/ZrO2-TiO2-SiO2Al2O3固体超强酸，并掺杂稀土元素钇、镧以及壳聚糖分别对其进行改性，利用其对丁酸己酯催化效能表征改性后的固体超强酸催化能力的变化。

会议

固体超强酸负载型催化剂掺杂改性

一种与软磁铁氧体成分共生的永磁铁氧体

本文介绍了一种与软磁铁氧体成分共生的永磁铁氧体的制作方法，通过能促进永磁铁氧体液相烧结的CaB2Si0.67O5.34添加剂的适量添加，获得了与组成式为CoFe2O4的软磁铁氧体成分共生的永磁铁氧体，磁体的显微结构、密度、磁性能均得到了显著的改善.

会议

共生软磁铁氧体永磁铁氧体

Study on the (Fe,Cr)7C3 particles reinforced ironbased composite coating

An iron based composite coating reinforced by (Fe,Cr)7C3 particles, with a thickness of 4.0 mm,was fabricated on the ductile castiron substrateby means of a centrifugal casting and in situ techniques.

会议

reinforcementIn situCompositecoating(FeCr)7C3

Study of xonotlite architectural coatings for exterior wall insulation mechanism

Thermal insulation exterior wall coating has been successfully prepared, using styrene-acrylic emulsion as film former, and xonotlite as heat-insulating filler,which produced by hydrothermal reaction.

会议

xonotlitecoatingsthermal insulationwallsmechanism

纳米镁粉对聚四氟乙烯热分解规律的影响

金属镁具有高反应活性，燃烧释放热值高，因此被广泛应用于火炸药领域。本文主要研究镁粉粒径及含量对聚四氟乙烯热分解的影响规律，选用两种不同粒度的镁粉进行对比，利用TG-DSC同步热分析仪研究不同升温速率下镁/聚四氟乙烯含能体系的热行为。

会议

热分解规律TG-DSC镁粉粒径含量

Preparation and Characterization of Mg-Doped GaN Nanowires by Au-Catalyzed Magnetron Sputtering Depo

Mg-doped GaN nanowires have been successfully synthesized on Si (111) substrates by magnetron sputtering deposition through ammoniating Ga2O3/Au thin films at 900 ℃ for 15 min.

会议

Mg-doped GaN nanowiresMagnetronsputtering depositionCatalystOptical property

Preparation and characteristic of different hollow microspheres filled syntactic foams

In this study, hollow glass microspheres (HGM) and hollow polystyrene microspheres (HPSM) have been employed as fillers in epoxy resin to prepare the syntactic foam.A kind of good performance composit

会议

Syntactic foamHollow glass microspheresHollow polystyrene microspheresMechani

Improved Photoluminescence and Vacuum Ultraviolet Irradiation Stability of Zn2SiO4∶Mn2+ with MgF2Nan

In order to prevent Zn2SiO4:Mn2+with short decay time for 3D plasma display panels (PDPs) from the deterioration of the luminescence efficiency caused by vacuum ultraviolet (VUV) irradiation, MgF2 coa

会议

Zn2SiO4∶Mn2+VUV degradationMgF23D plasma display panels

Preparation and Properties of Triazine Dithiol-Silane Composite Self-assembled hydrophobility Films

与本文相关的学术论文