5. Microstructure Analysis and Hydrogen Storage of Super Nanoporous Carbon Based on Corncob Particle Si

Microstructure Analysis and Hydrogen Storage of Super Nanoporous Carbon Based on Corncob Particle Si

来源 :第五届世界氢能技术大会(WHTC2013) | 被引量 : 0次 | 上传用户：sam008

【摘 要】

：

A super nanoporous carbon samples with BET surface area 3220 m2g-1,pore volume 1.64 cm3g-1 and sharp pore size distribution (< 5 nm) was prepared by adjusting activation process from corncob.And its h

【作 者】

：

Liu Xupeng Zhang Cunman Geng Zhen Ma Jianxin 

【机 构】

：

School of Automotive Studies,Tongji University,Shanghai 201804;Clean Energy Automotive Engineering C

【出 处】

：

第五届世界氢能技术大会(WHTC2013)

【发表日期】

：

2013年9期

【关键词】

：

Cornconb Particle Size Temperature Microporous carbon Mesoporous carbon Hydrogen 

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　A super nanoporous carbon samples with BET surface area 3220 m2g-1,pore volume 1.64 cm3g-1 and sharp pore size distribution (< 5 nm) was prepared by adjusting activation process from corncob.And its hydrogen adsorbed capacity was 1.23wt% at 100 bar and Room Temperature,6.18 wt% at 45 bar and -196 ℃.

其他文献

Improved de/hydrogenation properties of CeCl3+KH co-doped sodium aluminum hydride prepared by reacti

Sodium aluminum hydride (NaAlH4) is a suitable medium for solid-state hydrogen storage due to its relatively high hydrogen capacity (5.6 wt.%) and moderate temperature (100~150 ℃) and pressure (≤120 b

会议

Complex hydrideNaAlH4KHCeCl3DehydrogenationKinetics mechanism

Preparation of H2-permeable palladium membranes on porous stainless steel substrate modified by alum

会议

Photocatalyst of Hematite Doped with Tantalum for Water Splitting

会议

Development of a self-adaptive direct methanol fuel cell feeding with 20 M methanol

A passive and self-adaptive direct methanol fuel cell (DMFC) directly fed with 20 M of methanol is developed to ensure a high energy density of the DMFC.By using a polypropylene based pervaporation fi

会议

Core-shell Pd@Pt/C Catalyst for Oxygen Reduction Reaction

Methanol tolerant Pt-based oxygen reduction reaction (ORR) electrocatalyst are highly desirable for the direct methanol fuel cell (DMFC).[1] In this study,we report the synthesis of carbon-supported P

会议

Pd@Pt core-shelloxygen reduction reactiondirect methanol fuel cellmethanol to

Preparation of PtRu black electrocatalysts via sacrification of magnesia particle for methanol oxida

So far,synthesis of PtRu black catalyst with high alloying degree and small particle size still remains a big challenge for the practical application in the DMFC.In this work,PtRu black catalysts were

会议

direct methanol fuel cellPtRu blackmethanol oxidationPtRu alloys

Improved reversible dehydrogenation properties of the 2LiBH4-MgH2 composite by milling with metal-fr

The LiBH4-MgH2 reactive hydride composite is a promising hydrogen storage material due to the combined high hydrogen capacity and significant reduced reaction enthalpy.However,the sluggish de/rehydrog

会议

Hydrogen storageReactive hydride compositeCarbon nitrideBoron nitrideLayered

Hydrogen embrittlement of 304L austenitic stainless steel after catholically hydrogen charging: Effe

The effect of plastic pre-deformation on hydrogen embrittlement of 304L austenitic stainless steel was investigated by tensile testing.A group of flat tensile specimens were firstly strained to 3%,6%,

会议

Hydrogen embrittlementPre-strainAustenitic stainless steelCold work

Investigation of recoverable degradation of PEM Fuel Cell operated under drive cycle and different h

会议

PEMFCRecoverable degradationDrive cycleHumid condition

Enhanced stability of Pt nanoparticles on carbon supports

会议