5. Effect of Pressing on Mechanical and Superconducting Properties of Bi-2223 Bulks

Effect of Pressing on Mechanical and Superconducting Properties of Bi-2223 Bulks

来源 :第八届亚洲应用超导会议 | 被引量 : 0次 | 上传用户：asdfghjkb

【摘 要】

：

The superconducting,structural and mechanical properties of BSCCO bulk samples have been studied as a function of pressure by means of AC susceptibility,XRD and microhardness measurements,respectively

【作 者】

：

K(i)l(ic) A. Safran S. Asikuzun E. Ozturk O. 

【机 构】

：

Ankara University,Department of Physics,Tandogan,Ankara,06100,Turkey;Ankara University,Center of Exc

【出 处】

：

第八届亚洲应用超导会议

【发表日期】

：

2015年5期

【关键词】

：

BSCCO bulk sample AC susceptibility microhardness 

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　The superconducting,structural and mechanical properties of BSCCO bulk samples have been studied as a function of pressure by means of AC susceptibility,XRD and microhardness measurements,respectively.In this study,3 samples have been prepared.

其他文献

The transport AC loss analysis in YBCO coated conductors with and without a ferromagnetic substrate

The AC loss characteristic plays an important role for the use of YBCO coated conductors in the electrical power application like transformers,fault current limiters and transmission cables.This paper

会议

AC lossCoated conductorsFerromagnetic substrateH formulationFinite element m

Composition ratio and superconducting property of SmBCO Coated Conductor fabricated by RCE-DR proces

RCE-DR(Reactive Co-Evaporation by Deposition and Reaction) is the most promising process for real commercialization of coated conductor that is the fastest and high thruput process.GdBCO(GdBa2Cu3O7-y)

会议

Peculiar oxygen and copper isotope effects on the pseudogap formation temperature in underdoped to o

We investigate the pseudogap (PG) state and the peculiar oxygen and copper isotope effects on the PG onset temperature T* in cuprate superconductors with large and small Fermi surfaces within the pola

会议

Cuprate superconductorsUnconventional electron-phonon interactionsPolaronic ef

The fabrication of MgB2 nano-bridges by electron-beam annealing and FIB etching

100nm thin Mg/B precursor films were prepared on SiC substrates in ZZSX-500 vacuum coating machine and annealed by electron-beam which only took fractions of a second.In this paper the best condition

会议

Nano-bridgesSuperconducting MgB2 thin filmsElectron-beam annealingFIB

Splice joint of REBCO coated conductors by silver nano paste

In the fabrication of superconducting devices using REBCO coated conductors,splice joint is one of important issues.In this study,a novel splicing method with silver nano paste was tried to decrease c

会议

REBCO conductorjointsilver nano paste

Intergranular behavior of pulsed laser deposited YBCO thin films

YBa2Cu3O7-δ (YBCO) ceramic thin films were deposited by pulsed laser deposition on single crystal LaAlO3 (100) substrates in O2 partial pressure (PO2) from 400 to 500 mTorr and substrate temperature 7

会议

YBa2Cu3O7-δPulsed laser depositionHigh TC filmsCritical current densityJosep

Cable Fabrication Facility and Quality Assurance/Quality Control at Lawrence Berkeley National Labor

The Lawrence Berkeley National Laboratory (LBNL),situated in Berkeley,California,U.S.A.,was named after Ernest Lawrence,the Nobel Prize winner who invented the cyclotron particle accelerator.Since the

会议

Rutherford cablesuperconducting cableaccelerator magnetsquality assurancequa

Effect of the mole ratio of metal organic sources on the performance of MOCVD-deposited Gd0.5Y0.5Ba2

A home-designed MOCVD system has been employed to prepare Gd0.5Y0.5Ba2Cu3O7-δ (GdYBCO) thin films on LaMnO3/ epitaxial-MgO/ IBAD-MgO/ solution-deposition-planarization-Y2O3 buffered Hastelloy tapes,wh

会议

GdYBCOMOCVDoutgrowthscritical currentcritical current density

Effect of Hf Addition on Critical Current Density of Trifluoroacetate Metal Organic Deposition Deriv

The second-generation of high temperature superconducting wires or coated conductors (CCs),based on YBCO thin film technology,are confronted with a commercialization process.The performance of critica

会议

Critical current densityFlux pinning(YEu)Ba2Cu3.6O7-δTFA-MODHf addition

Microstructure and transport properties of yttrium-rich YBa2Cu3O7-δ thin films using low-fluorine me

The production rate of REBa2Cu3O7-δ (REBCO) films could be improved effectively using metal-organic deposition by reducing fluorine content of the precursor solution (CLF-MOD).To obtained high quality

会议

YBa2Cu3O7-δ (YBCO) coated conductorconventional low-fluorine metallorganic depo