【摘 要】
：
本文分两个部分论述了铝酸钡在实验室条件下的研制和其在铝酸钠溶液中的脱硫应用.首先,利用贵州省织金县储量丰富、品位高的重晶石和毒重石与自产氢氧化铝在一定温度下混合焙烧可以制得纯度达95﹪以上的可溶性铝酸钡.其次,该自制铝酸钡用于铝酸钠溶液脱硫时,与氢氧化钡脱硫相比有两大突出优点:一为铝酸钡与溶液中SO2-的结合能力强于CO,在某种条件下甚至不与CO反应,而氢氧化钡进入铝酸钠溶液时先表现为与CO的强烈
【机 构】
：
中国铝业贵州分公司轻金属研究所(贵州贵阳)
论文部分内容阅读
本文分两个部分论述了铝酸钡在实验室条件下的研制和其在铝酸钠溶液中的脱硫应用.首先,利用贵州省织金县储量丰富、品位高的重晶石和毒重石与自产氢氧化铝在一定温度下混合焙烧可以制得纯度达95﹪以上的可溶性铝酸钡.其次,该自制铝酸钡用于铝酸钠溶液脱硫时,与氢氧化钡脱硫相比有两大突出优点:一为铝酸钡与溶液中SO<,4><>2-的结合能力强于CO<,3><2->,在某种条件下甚至不与CO<,3><2->反应,而氢氧化钡进入铝酸钠溶液时先表现为与CO<,3><2->的强烈结合,排除SO<,4><2->的有效反应则滞后;二为铝酸钡的循环使用工艺简单,技术条件单一,原料单耗低,氢氧化钡的循环使用技术条件则较复杂.
其他文献
Serials of DyCo2-xGax alloys with x from O to 2 were prepared by arc melting and investigated by X-ray powder diffraction analysis．Four ternary compounds，DyCo1.33Ga0.67，DyCoGa,DyCo0.67-0.35Ga1.33-1.65
The influence of C and Al content on phase transformation temperatures, i.e. the Al and A3 of Fe-rich alloys is investigated by dilatometric analysis. With the new set of experimental data, an updated
The TbFe6-xGa6+x compounds (x=0，0.5，1.0 and 1.45)have been prepared and studied by X-ray powder diffraction and magnetization measurements．The structure of the compound TbFe6-xGa6+x transfers from the
A thermodynamic database on the phase equilibria of the uranium base alloys，including U-X(X：Al，Co，Cr,Cu，Ga,Mg，Mn，Mo，Nb，Th，W)binary system has been developed by the Calculation of Phase Diagrams(CALPHA
Nanostructuring is one of the effective approaches to lower the thermal conductivity of thermoelectric materials for improving its figure of merit．The nano-sized uniform skutterudite Co4-xNixSb12(x=0，
The 450℃ isothermal section of the Zn-Fe-Nb ternary system with an emphasis on the Zn-rich corner was experimentally determined by means of optical microscopy，SEM-EDS analysis and X-ray diffraction．A
The composition range of amorphous forming for Al-Fe-Zr system has been determined by mechanical alloying of mixture of elemental powders．The phases of as-milled powders were analyzed by XRD．The compo
It has been recognized that a substantial increase in the magnetostrietion of Fe occurs with the substitution of small amounts of non-magnetic elements, such as Ga and AI, for Fe. The magnetostriction
本文首先对喷气包缠纺和喷气涡流纺的加捻过程进行了描述，加捻过程的描述是成纱机理研究的基础。然后对喷气涡流纺纱成纱机理的自由端特征进行了分析，并利用PHOENICS软件对喷嘴中气流的运动进行了模拟，以及利用高速摄影对纤维加捻过程进行了拍摄，同时，结合成纱结构进一步说明了成纱机理。认为喷气涡流纺具有明显的自由端纺纱特征，但中心仍有未断裂的一定量的连续纤维，因此，喷气涡流纺可以看成是部分自由端纺纱、半自
本文对中州分公司2002年能源消耗情况进行了分析,阐述了通过开展设备经济运行和技术攻关活动使能源消耗大幅降低的经验,探讨下一步的节能途径,结合生产实际,提出熟料窑进行降低生料浆水分、稳定窑热工制度、提高煤磨出口温度、磨细生料煤是下一步的节煤方向,抓好常压脱盐、Ⅴ组Ⅵ组间接加热脱硅机和蒸发器的改造是下一步的节汽方向,抓好自发电量、提高功率因数和设备开停车的管理是下一步的节电方向,同时抓好生产稳定运行