Scrap leather fibers (SLFs) modified with the active silane containing epoxide groups (GPTMS) was incorporated into poly (lactic acid) (PLA) modified by vinyl trimethoxysilane was prepared for bio-com
【出 处】
：
2012 Postdoctoral Symposium of China on Materials Science &
论文部分内容阅读
Scrap leather fibers (SLFs) modified with the active silane containing epoxide groups (GPTMS) was incorporated into poly (lactic acid) (PLA) modified by vinyl trimethoxysilane was prepared for bio-composites by solvent compounding technology in this article.This study examined the effects of silane coupling agents on the structures of PLA and SLFs molecules, and the thermal properties, impacting strength, tensile strength and thermal stability of PLA/SLFs bi-composites also were measured.The results of fourier-transform infrared spectroscopy (FTIR) had proved that silane had been incorporated successfully to PLA and SLFs molecules by means of the solvent technology.Scanning electric microscopy (SEM) was used to investigate both the changes in shapes between the pristine SLFs and the treated SLFs and the microscopic structures of bio-composites.According to SEM results, it was shown that there were some significant differences between the untreated and treated SLFs, and a double continuous phase structure had occurred in PLA/SLFs bio-composite due to the excellent dispersion of SLFs in matrix.Differential scanning calorimetry (DSC) results displayed that the addition of SLFs into PLA had some significant effects on the crystallization behavior of PLA.However, Wide X-ray diffraction (WXRD) measurements had not significantly disrupted crystallization or altered the crystal structure within PLA.The addition of the treated SLFs into PLA resulted to the distinct improvement of the impact and tensile strengths.When the concentration of the treated SLFs was 15 pbw (parts by weight), the notched impact strength and tensile strengths of PLA/SLFs bio-composites were improved by 34.4% and 21.2% compared with the pristine PLA, respectively.Additionally, with increase of the modified SLFs content, the thermal stability of PLA/SLFs bi-composites was apparently improved.The macroscopic properties of bio-composites were found to be strongly dependent on their components, concentrations, dispersion and resulted morphological structures.
其他文献
The new generation hydro-cracking reactors are usually made of 2.25Cr-lMo-0.25V steel.After austenization at 940℃ of the hot-rolled sample, the study show that the microstructures of the steel after w
SiCp/2024Al composite foams were manufactured by powder metallurgical methods using foaming agent CaCO3.The fabrication technology of composite foams was researched, and their compressive properties a
To improve the fatigue performance of metal materials which are applied in the aeroplane structure is a significant objective of new material research.In recent decades, it becomes a common view that
This work aims to study the effect of sintering temperatures on the compressive strength and weight of net paste concrete.The compressive strength and quality variety of concrete which undergo differe
The quench sensitivity of a 6351 alloy was determined by time-temperature-transformation (TTT) curves and time-temperature-property (TTP) curves by an interrupted quench technique with the measurement
In traditional semi-rigid analysis of extended end plate connections is assumed to be deterministic parameters, most of moment-rotation models of the joint is determined by curve-fitting and statistic
Hygro-thermo-mechanical model is presented for investigating hygro-thermal defromation of concrete based on the coupling effect of multi-physical field and transfer mechanism of moisture and heat in p
This study seeks to develop a scientific understanding of the effects of dynamic loading history on the low-yield-strength shear panel damper (LYSPD) mechanical properties and fatigue performance.The
The cutting head cut teeth was under high pressure, the shear force and random wallop at its tunneling work, cut teeth in the cut process under the effect of random load, and accompanied by warming ph
3D four directional braided (SiO2)f/SiO2 composites were prepared by silicasol-infiltration-sintering method.The specimen density was determined to be 1.71 g/cm3 by using the Archimedes principle.The