【摘 要】
:
Copper has been proposed as a new material for metallization in Si-based semiconductor devices due to its low resistivity,high chemical stability,and excellent electromigration resistance.In this pape
【机 构】
:
School of Materials Science and Engineering,Southwest Jiaotong University,Key Laboratory of Advanced
【出 处】
:
2015 Shanghai Thin Film Conference(2015上海薄膜国际会议)
论文部分内容阅读
Copper has been proposed as a new material for metallization in Si-based semiconductor devices due to its low resistivity,high chemical stability,and excellent electromigration resistance.In this paper,in order to improving the properties of Cu thin films further,the films were deposited on Si(100)substrate with different bias voltage by high power pulsed magnetron sputtering(HPPMS).
其他文献
Three dimensional highly hierarchical flower-like Bi2WO6 microspheres self aggregated by nanoplates have been fabricated in a green hydrothermal way at low temperature,without using any template or se
Resorcinol-formaldehyde (RF) and graphene-oxide (GO) gels have a variety of applications due to their excellent and remarkably flexible properties.[1,2] Despite a lot of efforts,there are still great
The hierarchical assembly of inorganic and organic building blocks is an efficient strategy to produce high performance materials which has been demonstrated in various biomaterials.[1,2] In the past
以氧化石墨烯、正硅酸四乙酯和苯胺单体为原料,采用两步法制备了石墨烯/二氧化硅/聚苯胺三元复合材料.采用循环伏安法对材料进行电化学性能测试[1],结果表明,当氧化石墨烯与苯胺单体的投料比为1:50时,在1 MH2SO4电解液中,在扫描速度1 mV/s下,三元复合材料的比容量达554.5 F/g,远大于石墨烯/二氧化硅的比容量(144 F/g).
The development of environment-friendly and high energy density cathode materials is highly desired for the clean and sustainable Li-ion batteries (LIBs) system.To take advantage the effect of oxygen-
The atomic layer deposition (ALD) technique is a surface-controlled and layer-by-layer process,relying on two sequential self terminating half-reactions,offering unmatched precision in terms of contro
Nowadays,although Li ion battery technology is sufficient to power small portable devices such as mobile phones and lap-top computers,significant challenges in the specific capacity and rate capabilit
锂离子电池使用的正极材料多为可逆脱/嵌锂离子的层状氧化物,传统正极材料如LiCoO2、LiNiO2等存在着各种不可避免的缺点,LiCoO2实际放电比容量较低、成本高、毒性大,LiNiO2热稳定性和结构稳定性较差[1].三元材料LiNixCoyMn1-x-yO2是三种层状氧化物不同比例混合的固溶体,具有比容量高、循环性能好、成本低、环境友好等优点,近年来受到广泛的关注和研究.
本文将溶胶-凝胶法与共沉淀法相结合,探索出了一种液相制备NCA材料新方法.SEM测试结果表明制备出的Ni0.85Co0.12Al0.03(OH)2前躯体为8-12μm球形颗粒,其表面为细丝状,经溶胶法锂化高温烧结得到NCA材料仍为球形颗粒,颗粒平均粒径为8-12μm,其表面则为多面体结构.充放电测试结果表明该材料在2.75-4.25V电压范围内,0.1C电流密度下,放电比容量高达196mAh/g.
Recently,2D materials,such as graphene,MoS2,TaSe2 and WS2,have received great research interests due to their unique electronic,optical,and chemical properties.Mica is a well-known layered silicate co