【摘 要】
：
Supplementary cementitious materials (SCMs) like fly ash (FA) and blast furnace slag (BFS) are normally used to replace parts of Ordinary Portland cement (OPC) to reduce the cost and CO2 emission.Some
【机 构】
：
Microlab, Delft University of Technology, 2628 CN, Delft, The Netherlands
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
Supplementary cementitious materials (SCMs) like fly ash (FA) and blast furnace slag (BFS) are normally used to replace parts of Ordinary Portland cement (OPC) to reduce the cost and CO2 emission.Some consequences are the reduction of portlandite (CH) content and the formation of C-S-H with low Ca/Si ratio, due to pozzolanic reactions.It is known that carbonation of portlandite leads to a reduction in the porosity which is ascribed to the positive difference of molar volumes between CH and CaCO3.However, the influence on the porosity caused by the carbonation of C-S-H is still controversial.The molar volume change due to the carbonation of C-S-H depends on the properties of C-S-H (like Ca/Si ratio, water content) and the water remained in silica gel.Moreover, the decalcification of C-S-H with the Ca/Si ratio lower than 1.2 can cause more structure changes and shrinkage of C-S-H.During the carbonation of cement paste blended with SCMs, less portlandite but a relatively high amount of C-S-H with low Ca/Si ratio will be carbonated.The pore structure will evolve in a different way, comparing with Portland cement paste.Therefore, its very important to figure out the pore structure development of cement paste blended with SCMs under carbonation.
其他文献
This work presents characterization of slag cements and modified oxygen steelmaking slags by pyrometallurgical process.Chemical analysis, SEM and quantitative mineralogical XRD analysis using Rietveld
During the past decadc;blended cements have attracted strong interest worldwide due to their advantages of low energy cost, high strength and good durability.A major incentive for further development
Portland cement is considered one of the most important construction materials in the world due to, for instance,the mechanical and durability behaviour.However, the industrial production of Portland
Series of cementitious binders with potential application in oil and geothermal wells were developed.Commercial G-oil cement modified by adding blast furnace slag and silica fume, fiber-reinforced cem
Blast furnace slags are added to Portland cements for environmental / economic reasons as well as for durability interests.When reaching high levels of cement replacement, mechanical strength of these
It had gained wide acknowledgement that some phosphor and fluorine released from phosphorus slag had caused the set-retarding and low early-strength of cement and concrete with yet no solid explanatio
Ii is an important way of achieving steel slag large-scale effective utilization that steel slag used as the supplementary cementitious materials.However, the activity of steel slag is very low, it is
It has great potential that steel slag powder as the supplementary cementitious materials used in cement and concrete field.Cementitious property of steel slag powder and effect of its fineness and in
Metallurgical slags are produced in a very large amount in pyrometallurgical processes and are huge sources of waste if not properly recycled and utilized.This study reports the effect of fine ground
Dispersed sufficiently silica fume is able to realized its filling effect and secondary reaction of hydration better,a new dispersing method on silica fume aiming to dispersing silica fume fully is in