CNFs on Graphite FeltA Potential Catalyst for Ozonation

来源 :4th International Symposium on Carbon for Catalysis(第四届国际碳催化 | 被引量 : 0次 | 上传用户：lilianmm

【摘 要】

：

　　Carbon nanofibers (CNFs) supported on graphite felt were tested in the ozonation of oxalic acid.The best performance was observed for the untreated sample,

【作 者】

：

Estelle Vanhaecke Magnus R(o)nning De Chen Jo(a)o Restivo José J.M.(O)rf(a)o M.Fernando R.Pereira 

【机 构】

：

ChemicalEngineeringDepartment,NTNU,SemS(oe)landsvei4,7193TrondheimNorwayLaboratóriodeCatáliseeMateri

【出 处】

：

4th International Symposium on Carbon for Catalysis(第四届国际碳催化

【发表日期】

：

2010年11期

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Carbon nanofibers (CNFs) supported on graphite felt were tested in the ozonation of oxalic acid.The best performance was observed for the untreated sample, showing that this material is a potential catalyst for ozonation.The presence of oxygen-containing surface groups has a detrimental effect on the catalytic activity.

其他文献

Preparation and Quantitative Characterization of Nitrogen-Functionalized Multi-walled Carbon Nanotub

　　Some important industry reactions can be catalyzed efficiently by carbon nanotubes with modified functionality [1].The doping of nitrogen into a graphitic s

会议

The Closed Ring Pair Metamaterials at Terahertz Frequencies

会议

A robust frequency comb of spanning from 0.4 to 4.2μm based on 7fs Tisapphire laser with monolithic

会议

Nanosize structural modifications and photoinscription of polarization sensitive devices in bulk sil

会议

Wavelength Scaling Law of Ellipticity Dependence of High-order Harmonic Generation

会议

Carbon Nanotubes Supported Highly Dispersed Ruthenium Catalysts by Facile Microwave Thermolytic Meth

会议

Catalytic Potential of Carbon-Silica Composite Materials

会议

Real-time observation of dynamic coupling between stretching and bending modes using a few-cycle pul

会议

Synthesis of Nitrogen Containing Carbon Nano Fibers and the Influences of Nitrogen Amount on the Ele

　　Nitrogen doped carbon nano fibers were prepared through a CVD method [1], in which Ni Fe alloy acts as catalyst.EELS mapping (Figure 1) shows a small amount

会议

Generation of wavelength switchable optical short pulses for the generation and modulation of Terahe

　　Double wavelength optical short pulse generation with high wavelength stability using one oscillating cavity to share the same gain medium has many advantag

会议