A new kind of emulsion containing nano TiO_2 was developed through the dispersion experiment. A commercial emulsion and a prepared by our lab emulsion without nano particles were chosen as controls to test the tribological and antibacterial properties of this new emulsion. The load carrying capacity, friction coefficient and average diameter of wear scars were tested by a four-ball machine and the comprehensive antifriction parameter ω was calculated. The wetting angle was also tested using a JC200C1 wetting angle tester. The micro surface and roughness of rolled strips were analyzed to investigate the tribological performance of the recommended new emulsion in strip production. It is shown that the new nano-emulsion possesses a higher load carrying capacity and wetting ability. Therefore the abrasive/plowing wear is reduced more efficiently with the addition of nano particles, and the micro surface is improved. The density of bacteria in the emulsions was tested after the cold rolling experiment. The emulsion breaking ratio and bacteria density were also tested in different time intervals after the cold rolling experiment. The final p H values and bacteria density of different layers of emulsions were measured and the sediment was analyzed by TEM to evaluate the antibacterial behavior of this new emulsion. It is shown that the density of microbial colonies which led to a corruption of emulsions was decreased about 90% and the effective antibacterial period was prolonged. A new kind of emulsion containing nano TiO 2 was developed through the dispersion experiment. A commercial emulsion and a prepared by our lab emulsion without nano particles were chosen as controls to test the tribological and antibacterial properties of this new emulsion. The load carrying capacity, friction coefficient and average diameter of wear scars were tested by a four-ball machine and the comprehensive anti friction parameter ω was calculated. The wetting angle was also tested using a JC200C1 wetting angle tester. The micro surface and roughness of rolled strips were analyzed to investigate the tribological performance of the recommended new emulsion in strip production. It is shown that the new nano-emulsion possesses a higher load carrying capacity and wetting ability. Therefore the abrasive / plowing wear is reduced more efficiently with the addition of nano particles, and the micro The density of bacteria in the emulsions was tested after the cold rollin g experiment. The emulsion breaking ratio and bacteria density were also tested in different time intervals after the cold rolling experiment. The final p H values ​​and bacteria density of different layers of emulsions were measured and the sediment was analyzed by TEM to evaluate the antibacterial behavior of this new emulsion. It shows that the density of microbial colonies which led to a corruption of emulsions was decreased about 90% and the effective antibacterial period was prolonged.