【摘 要】
：
分析了ＷＰ７乙系列发动机Ⅰ级涡轮叶片延伸段断裂的性质和原因。通过对断裂叶片的材质、热工艺、装配间隙的复查和断口的宏观、微观分析，证明叶片延伸段的断裂属于高周疲劳断裂；断裂
论文部分内容阅读
分析了ＷＰ７乙系列发动机Ⅰ级涡轮叶片延伸段断裂的性质和原因。通过对断裂叶片的材质、热工艺、装配间隙的复查和断口的宏观、微观分析，证明叶片延伸段的断裂属于高周疲劳断裂；断裂的内在原因是延伸段靠叶背一侧第５、６孔处存在较高的应力集中，外在原因是叶冠总间隙过大，阻尼效果差，引起叶片振动，导致疲劳断裂。
The nature and causes of the rupture of Grade I turbine blade of WP7 B series engine were analyzed. Through the review of the material, the thermal process and the assembly clearance of the broken blade and the macroscopical and microscopic analysis of the fracture, it is proved that the fracture of the blade extends to the high-cycle fatigue fracture. The internal cause of the fracture is the extension of the fifth, There is a high stress concentration in the hole. The external reason is that the total clearance of the blade crown is too large, the damping effect is poor, causing the blade to vibrate, resulting in fatigue fracture.
其他文献
α，β┐受体激动剂及白细胞对再灌注心律失常及室颤影响的正交分析戴德哉，安鲁凡，黄丹阳，孙瑞元．中国药理学报，１９９６，１７（２）：１４８目的：比较白细胞（Ｌｅｕ），α－受体激动（α－Ａｇｏ）和β－受体激动（β－Ａｇｏ）三因素对缺血－再灌诱发的心
可以预见，我国即将实行的处方药（RX）和非处方药（OTC）分类管理，对医院药学、医院药房乃至医院药学人员必然会带来一次巨大的冲击和引起一系列的变化。面临这些挑战，我们应该抓住这次
对265中镍铬冷硬铸铁轧辊铸态、热时效态和自然时效态的残余应力进行了测试，并分析了测试结果和分布规律。
The as-cast, hot-aging and natural-aging residual stresses of
我国加入WTO以后,欧盟等茶叶进口国对进口茶叶的农药残留标准要求更加严格,茶叶出口形势严峻。农药残留是导致我国茶叶行情一路下跌的重要原因,其中受害最大的是茶农。因此,
击风搏浪弄大潮忠心赤胆谱新篇──记湖北省随州市科技物资器材公司总经理王靠山同志柳敏煌，程国祥（湖北省随州市科委邮编；４４１３００）在被当代人称为“世界第八大奇迹”的曾侯乙编钟的故乡
心底无私天地宽─—记大同市税务二分局局长刘武本刊记者高士军作为科级干部，论官，充其量不过是一点尾巴梢子官，不大；作为基层税务部门一把手，论权，刘武守着税收执法关口，况且税务二
The authors generalized the methods how to identify and evaluate gas zones using logs,and put forward the methods of crossplots and overlays of porosity logs on
试论医院药品价格管理刘跃林潘伟（江苏省如皋市中医院２２６５００）薛娟娟（江苏省如皋市物价局）市场经济的形成给医院卫生事业带来生机和活力，保障了临床药品的供应。但给药品价格带来负效应，医
本文证明了,若选定与群键(SO_3D_nC_n)×SU(2)对称性相匹配的单电子基矢,则由它们直积构成的单个Slater函数是d~N体系D_nC_n旋量群不可约表示的基矢,或其2个一维表示直和的基