Formation Mechanism of Lamellar M23C6 Carbide in a Cobalt-Base Superalloy During Thermal Exposure at

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:sycamorelee
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The precipitation of the lamellar-shaped M23C6 carbide within the dendritic matrix of a cobalt-base superalloy during thermal exposure at 1000 ℃ has been investigated.Such a precipitation is not commonly observed in cobalt-base superalloys.It is found that M23C6 particles nucleate preferentially at stacking faults (SFs) in the dendritic matrix and grow along the SFs to develop a lamellar character.Additionally,a Cr depletion zone is observed in the vicinity of the lamellar M23C6 carbide,which strongly supports the presence of Suzuki segregation.
其他文献
Nanocrystalline and amorphous NdMg12-type NdMg11Ni +x wt% Ni (x=100,200) alloys were successfully prepared through ball milling (BM).The microstructures and electrochemical properties were systematically studied to get a more comprehensive understanding o
The effect of phosphorus on the precipitations of γ“,γ\'and δ phases and associated tensile properties in IN718C alloy are investigated in this study.It is revealed that P atoms are dissolved in the grain interior to a relatively high degree and hence i
In order to study the influence of the physical state of solder on the interfacial reaction of dip-soldered Sn-3.0Ag-0.5Cu/Cu system,two kinds of experiments were designed,including:(1) solid-state aging between the solder and Cu substrate;(2) liquid-stat
Direct laser metal deposition is a kind of advanced rapid manufacturing technology,which can produce near net shape parts by depositing metal powders layer by layer.This study demonstrates fabrication,the anisotropy of mechanical properties and hardness o
The influences of pin offset on the formation,microstructure and mechanical properties of friction stir welded joint of Ti6A14V and AZ31B Mg dissimilar alloys were investigated.The results show that sound joints are obtained at different offsets.With the
The microstructures and corrosion behavior of AlSi5Cu 1Mg alloy modified with different contents of La were investigated.Optical microscopy observations showed that the microstructures of AlSi5Cu 1Mg-xLa (x =0,0.3,0.6,and 0.9 wt%) alloy transformed from c
With the aim of improving corrosion resistance of rod cladding for in-service and accident conditions,six new zirconium alloys (named N1-N6) have been designed.The contents of Sn and Nb were optimized for better behavior at high-temperature pressurized wa
In the present study,creep activation energy for rupture was obtained as 221-348 kJ/mol for 22Cr15Ni3.5CuNbN due to the precipitation-hardening mechanism.The extrapolation strength of creep rupture time of 105 h at 923 K for 22Cr15Ni3.5CuNbN is more valid
The corrosion behaviors of X65 steel in the artificial seawater at different hydrostatic pressures are investigated by potentiodynamic polarization measurements,electrochemical impedance spectroscopy measurements and weight loss measurements.The corroded