Creep Behavior and Life Assessment of a Novel Heat-Resistant Austenite Steel and Its Weldment

来源 :金属学报(英文版) | 被引量 : 0次 | 上传用户:pingpingkama
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
In the present study,creep activation energy for rupture was obtained as 221-348 kJ/mol for 22Cr15Ni3.5CuNbN due to the precipitation-hardening mechanism.The extrapolation strength of creep rupture time of 105 h at 923 K for 22Cr15Ni3.5CuNbN is more valid (83.71 MPa) predicted by the Manson-Haferd method,which is superior to other commercial heat-resistant steels.The tensile creep tests ranging from 180 to 240 MPa at 923 K were conducted to investigate creep deformation behavior of welded joint between a novel heat-resistant austenite steel 22Cr15Ni3.5CuNbN and ERNiCrCoMo-1 weld metal.Apparent stress exponent value of 6.54 was obtained,which indicated that the ratecontrolled creep occurred in weldment during creep.A damage tolerance factor of 6.4 in the weldment illustrates that the microstructural degradation is the dominant creep damaging mechanism in the alloy.Meanwhile,the welded joints perform two types of deformation behavior with the variation in applied stress,which resulted from the different parts that govern the creep processing.Also,the morphology evolution of the fracture surfaces confirms the effects of stress level and stress state.
其他文献
The residual stress evolution in a safe-end/nozzle dissimilar metal welded joint of CAP1400 nuclear power plants was investigated in the manufacturing process by finite element simulation.A finite element model,including cladding,buttering,post-weld heat
The effects of Ni content and ball milling time on the hydrogen storage thermodynamics and kinetics performances of asmilled La5Mg95-xNix(x =5,10,15) ternary alloys have been investigated.The evolution of microstructure and phase of experimental alloys in
A large amount of directional and willow-like β\'phase was precipitated in Mg-10Gd-3Y-0.4Zr (GW103K) alloy after solution treatment and subsequently aged treatment (T6).In order to explore the effect of the precipitates on the corrosion behavior of the
Nanocrystalline and amorphous NdMg12-type NdMg11Ni +x wt% Ni (x=100,200) alloys were successfully prepared through ball milling (BM).The microstructures and electrochemical properties were systematically studied to get a more comprehensive understanding o
The effect of phosphorus on the precipitations of γ“,γ\'and δ phases and associated tensile properties in IN718C alloy are investigated in this study.It is revealed that P atoms are dissolved in the grain interior to a relatively high degree and hence i
In order to study the influence of the physical state of solder on the interfacial reaction of dip-soldered Sn-3.0Ag-0.5Cu/Cu system,two kinds of experiments were designed,including:(1) solid-state aging between the solder and Cu substrate;(2) liquid-stat
Direct laser metal deposition is a kind of advanced rapid manufacturing technology,which can produce near net shape parts by depositing metal powders layer by layer.This study demonstrates fabrication,the anisotropy of mechanical properties and hardness o
The influences of pin offset on the formation,microstructure and mechanical properties of friction stir welded joint of Ti6A14V and AZ31B Mg dissimilar alloys were investigated.The results show that sound joints are obtained at different offsets.With the
The microstructures and corrosion behavior of AlSi5Cu 1Mg alloy modified with different contents of La were investigated.Optical microscopy observations showed that the microstructures of AlSi5Cu 1Mg-xLa (x =0,0.3,0.6,and 0.9 wt%) alloy transformed from c
With the aim of improving corrosion resistance of rod cladding for in-service and accident conditions,six new zirconium alloys (named N1-N6) have been designed.The contents of Sn and Nb were optimized for better behavior at high-temperature pressurized wa