The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test(SSRT), the stress corrosion cracking(SCC) behaviors of S355 steel under the different strain rates in the solution were investigated, and the fracture morphologies and compositions of corrosion products under the different strain rates were analyzed with scanning electron microscopy(SEM) and energy dispersive spectrometerry(EDS), respectively. The experimental results show that the SCC sensitivity index is the highest when the strain rate is 2×10-6, and the medium corrosion is the main reason resulting in the highest SCC sensitivity index. The SCC sensitivity index is the least when the strain rate is 5×10-6, and the stress is the main reason resulting in the stress corrosion. The SCC sensitivity index is the middle when the strain rate is 9×10-6, the interaction of stress and medium is the stress corrosion fracture mechanism. The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test (SSRT), the stress corrosion cracking (SCC) behaviors of S355 steel under the different strain rates in the solution were investigated, and the fracture morphologies and compositions of corrosion products under the different strain rates were analyzed with scanning electron microscopy (SEM) and energy dispersive spectrometerry (EDS), respectively. The experimental results show that the SCC sensitivity index is the highest when the strain rate is 2 × 10-6, and the medium is the main reason that the highest SCC sensitivity index. The SCC sensitivity index is the least when the strain rate is 5 × 10-6, and the stress is the main reason resulting in the the stress corrosion. The SCC sensitivity index is the middle when the strain rate is 9 × 10 -6, the interaction of stress and medium is the stress corrosion fracture mechanism.