对20~#钢表面裂纹的看法

来源 :包钢科技 | 被引量 : 0次 | 上传用户:lnlsq
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
国内一些小型钢厂用20~#钢小钢锭直接轧制钢管时,表面产生裂纹的现象很严重。包钢的20~#钢管是由管坯轧制,表面裂纹不明显,但在钢坯上时有发生,其产生的原因长期未决。 20~#钢表面裂纹敏感性是多年来国内外许多人都在研究的问题。近几年在国内金相会议上对20~#钢表面裂纹的问题也进行了几次讨论,初步认为20~#钢表面的缺陷是导致表面裂纹的主要原因之一。这些表面缺陷,如皮下气泡,夹杂和凹坑等,在加热时氧化,轧制中受力开裂。我们过去的许多检验 Some domestic small mills with 20 ~ # small steel ingot direct rolling steel, the surface cracks are very serious. Baotou 20 # steel pipe is rolled by the tube, the surface cracks are not obvious, but sometimes occur on the billet, the reasons for its long-pending. 20 ~ # steel surface crack sensitivity over the years many people are studying the issue. In recent years, the domestic metallurgical conference on the 20 ~ # steel surface cracks have also been discussed several times, initially that 20 ~ # steel surface defects is one of the main causes of surface cracks. These surface defects, such as subcutaneous bubbles, inclusions and pits, etc., in the heating oxidation, rolling stress cracking. Many of our past tests
其他文献
主题为“华商携手新世纪,和平发展共繁荣”的第六届世界华商大会将于2001年9月在南京召开,届时来自全世界的4000多名华商将聚会南京。为此,全国政协副主席、全国工商联主席、第六届世界华
编者按:欧盟是我国最重要的贸易合作伙伴之一。据统计资料显示1999年我国出口欧洲的产品价值为557亿美元比上年增长5.5%预计中欧贸易增长还将逐渐加大双方贸易往来会出现高速发
缉 私警察组建一年多来 ,积极履行党和人民赋予的神圣职责 ,取得了举世瞩目的辉煌战绩 ,有力地保卫了祖国的经济长城 ,走私犯罪分子为之闻风丧胆。然而 ,战斗刚刚开始 ,打私
从不在王宫中过夜萨达姆必须偷着睡觉,必须不停地变换睡觉的时间与地点,不断地从一张床转到另一张床。他几乎从不在他的王宫中过夜。睡觉和固定的例行公事成为他难得的享受
1.前言在热轧无缝钢管生产中,为得到具有一定尺寸精度和真圆度的成品管需进行定径。如尚若较大的减少外径,通常采用单架减径率和总减径率皆较定径大得多的减径生产技术。在
常用CrWMn钢冷作模具,工作时损坏,往往不是因强度、硬度不足,耐磨性不够,而是韧性差引起脆性断裂造成的。为此我们对手表厂CrWMn钢冷冲模进行了循环热处理,其工艺如图1所示
热轧铝板带材用乳化液润滑的主要目的是防止铝的粘结和冷却,控制辊型。它以水溶性油为基础油和乳化剂等其他添加剂组成,属水包油(O/W)型乳液。本文介绍了近年来美国、日本、
应用Formastor全自动相变测量仪测定了适用退火的7Cr7Mo3V2Si钢的T.T.T.曲线。根据这一T、T、T曲线详细地研究和分析了退火工艺参数对退火效果的影响,进而得出两种最佳的退火
使用计量语言学和文本分析的方法,梳理、阐释“文凭”一词在清晚期古今词义的嬗变可见:一方面,“文凭”一词最早在唐代文献中已有使用,但其“毕业证书、学历证明”这一近现代
近几年发展最快、国际化程度最高的城市,毋庸质疑是上海,从浦东的飞速发展到 APEC 会议的召开,甚至连香港都开始怀疑自己的亚洲地位是否会被上海替代。那么在房地产方面,上海