The lanthanum ricinoleate(abbreviated as Lari3) of rare earth heat stabilizer was synthesized by the reaction of ricinoleic acid, lanthanum nitrate and sodium hydroxide. The IR and fluorescence spectra methods confirmed the structure of the product. The thermal stability of PVC in the presence of Lari3 was studied by the Congo method and using TG analysis. The results showed that Lari3 could be used as a thermal stabilizer for PVC. When the ratio of Lari3/pentaerythritol was 3:1, the complex exhibited better synergistic effect. Incorporation of Lari3 to PVC resulted in a marked increase of maximum and onset degradation temperature as well as elongation and impact strength of PVC. Lari3 might replace the labile chlorine atoms to interrupt the formation of conjugated double bonds in PVC chains and act as HCl scavenger to restrain the self-catalyticdehydrochlorination.
The lanthanum ricinoleate (abbreviated as Lari3) of rare earth heat stabilizer was synthesized by the reaction of ricinoleic acid, lanthanum nitrate and sodium hydroxide. The IR and fluorescence spectra methods the structure of the product. The thermal stability of PVC in the presence of Lari3 was studied by the Congo method and using TG analysis. The results showed that Lari3 could be used as a thermal stabilizer for PVC. When the ratio of Lari3 / pentaerythritol was 3: 1, the complex said better synergistic effect. Incorporation of Lari3 to PVC resulted in a marked increase of maximum and onset temperature as well as elongation and impact strength of PVC. Lari3 might replace the labile chlorine atoms to interrupt the formation of conjugated double bonds in PVC chains and act as HCl scavenger to restrain the self- catalyticdehydrochlorination.