In Fe-20Cr-4Al-Y alloys with （0.13～0.73） wt% Y,Y-containing phase was observed.Its Y content andcrystal structure were identical with those Of YFe<sub>9</sub> phase basically,and microhardness was 4～5 times higherthan that of α-phase matrix.Th