By means of chemical reduction,nanoparticles of platinum were deposited on the surface of multi walled carbon nanotubes (MWCNTs).The performance of hydrogen storage of as prepared MWCNTs decorated with platinum was investigated.The results indicate that:(1) Hydrogen uptake is more quick and intense for decorated MWCNTs than that for not decorated ones at 10.931MPa and room temperature.The saturation of hydrogen uptake of the former only lasts about 30min,while the latter needs about 150 min;(2) The amount of hydrogen uptake of decorated MWCNTs is about 1.13wt%, which is larger than that of not decorated ones(about 0.54wt%);(3) However,more than 37% hydrogen absorbed by decorated MWCNTs is chemisorbed.
By means of chemical reduction, nanoparticles of platinum were deposited on the surface of multi walled carbon nanotubes (MWCNTs). The performance of hydrogen storage of as prepared MWCNTs decorated with platinum was investigated. The results indicate that: (1) Hydrogen uptake is more quick and intense for decorated MWCNTs than that for not decorated ones at 10.931MPa and room temperature. saturation of hydrogen uptake of the former only lasts about 30min, while the latter needs about 150 min; (2) The amount of hydrogen uptake of decorated MWCNTs is about 1.13 wt% which is larger than that of not decorated ones (about 0.54 wt%); (3) However, more than 37% hydrogen absorbed by decorated MWCNTs is chemisorbed.