In the reaction of mathane, carbon dioxide with oxygen to synthesis gas, conversion ofCH4 was increased, but CO selectivity was reduced when CeO2 was added to Ni/CaO-Al2O3catalyst The characterization of TPR, XPS. XRD and H2-TPD exhibited that, on one hand, theCeO2 promoter decreased the reduction temperature of catalyst. On the other hand, addition ofCeO2 resulted in an increase in the electron density of active component Ni, and as a result,reduced the ability of CH4 deep cracking and enhanced the resistance to carbon-deposition ofcatalyst. In addition, the existence of CeO2 was beneficial to decrease the Ni crystal particle size.
On the reaction of mathane, carbon dioxide with oxygen to synthesis gas, conversion of CH4 was increased, but CO selectivity was reduced when CeO2 was added to Ni / CaO-Al2O3catalyst The characterization of TPR, XPS. XRD and H2-TPD injection that, on one hand, theCeO2 promoter decreased the reduction temperature of catalyst. On the other hand, addition ofCeO2 resulted in an increase in the electron density of active component Ni, and as a result, reduced the ability of CH4 deep cracking and enhanced the resistance to carbon In addition, the existence of CeO2 was beneficial to decrease the Ni crystal particle size.