Preparation and properties of metal-PVA composite hydrophilic ultrafiltration membranes

来源 :Journal of Central South University of Technology(English Ed | 被引量 : 0次 | 上传用户:aqcnbbz1
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Metal-polyvinyl alcohol(PVA) composite ultrafiltration membranes were prepared by coating a certain concentration of PVA solution on metallic fiber sintered membranes. The effects of preparation conditions, such as the coating solution concentration, sequence and times of coating, and heat-treatment on the properties of the composite membranes were studied. The results show that the hole diameter of the composite membrane decreases with the increase of the concentration of PVA, the hole diameter of composite membrane is different when the sequence of coating is different. When the higher concentration of PVA solution is used to coat the metallic membrane for the first time and the other smaller one for the second time, the hole diameter of the composite membrane is relatively small, compared with that of the composite membrane made by the smaller concentration of PVA solution for the first time and the other higher one for the second time. The holes of the composite membrane contract and the stability of the membrane is improved by heat treatment. When metal-PVA composite hydrophilic membranes are used to treat the oil/water emulsion with the concentration of 1 000 mg·L -1 , the retention is from 80% to 90%, and the permeate flux is from 15 L·m -2 ·h -1 to 40 L·m -2 ·h -1 at pressure of 0.2 to 0.3 MPa. The effects of preparation conditions, such as the coating solution concentration, sequence and times of coating, and heat-treatment on the properties of the composite membranes were studied. When the hole diameter of the composite membrane decreases with the increase of the concentration of PVA, the hole diameter of composite membrane is different when the sequence of coating is different. of PVA solution is used to coat the metallic membrane for the first time and the other smaller one for the second time, the hole diameter of the composite membrane is more small, compared with that of the composite membrane made by the smaller concentration of PVA solution for the first time and the other higher one for the second time. The holes of the composite membrane contract a nd the stability of the membrane is improved by heat treatment. When metal-PVA composite hydrophilic membranes are used to treat the oil / water emulsion with the concentration of 1000 mg · L -1, the retention is from 80% to 90% and the permeate flux is from 15 L · m -2 · h -1 to 40 L · m -2 · h -1 at pressure of 0.2 to 0.3 MPa.
其他文献
The pure iron was melted and deoxidized by metallic Al and rare earth elements La, Ce and Y respectively at 1600℃ in avertical resistance furnace. The morpholo
给出了一种基于多个样本单元或给定标准的多目标、多准则综合评价方法 ,并讨论了它的相关性质 .同时 ,还给出了一种依据样本前沿面移动划分可行集的算法 ( MSF) .根据划分的
A new hot-rolled low alloy high strength steel with grain boundary allotriomorphic ferrite/granular bainite duplex micro-structure has been developed through no
CdS nanoclusters were synthesized by using n- octylthiol as a ligand and n- hexadecyl- trimethyl-ammonium bromide (or n-tetrabutylammonium bromide) as an organi
The study concentrates mainly on the development of failure process in composite rock mass. By use of acoustic emission(AE), convergence inspection, pressure mo
An automatic monitoring technique of the seepage line, including the monitoring design, the automatic monitoring system and the backfill technique of the measur
BaFe12O19 hexaferrites were prepared by citrate sol-gel process. The formation temperature was much lower thanthat of the conventional ceramic method. The compl
The stripping and regeneration of the loaded organic phase of phosphorous mixer extractant (PPD) were studied.The mixed solutions (3 mol/L HCl +2 mol/L ZnCl2) w
The effect of transverse coupling in a photorefractive oscillator is studied. From the study the condition for stable optical patterns of multimode oscillation
The MAO (Micro-Arc Oxidation) process is applied to a eutectic Al-Si alloy (Al-12.0%Si-l.0%Cu-0.9%Mg(mass fraction)). The oxide ceramic layer was fabricated wit