我厂采用QT60-2铸造水泵叶轮,生产中废品率较高,主要缺陷为缩松,发生部位在上下平面与叶片交叉的热节处。此项缺陷约占废品的70％。我们曾进行了加大冒口与下面设冷铁等工艺试
论文部分内容阅读
我厂采用QT60-2铸造水泵叶轮,生产中废品率较高,主要缺陷为缩松,发生部位在上下平面与叶片交叉的热节处。此项缺陷约占废品的70％。我们曾进行了加大冒口与下面设冷铁等工艺试验,由于工艺比较复杂,而且易导致气孔和裂纹缺陷增加,问题未能得到解决。1983年改成硬模铸造,经两年多的生产实践,取得比较显著的效果。
I plant using QT60-2 casting pump impeller, the production of high rejection rate, the main defect is shrinkage, the occurrence of parts in the upper and lower plane at the hot section of the intersection of leaves. This defect accounts for about 70% of the scrap. We have carried out a larger riser and the following test set of cold iron and other processes, due to the complexity of the process, and easily lead to increased porosity and crack defects, the problem can not be solved. In 1983 into a die casting, after more than two years of production practice, achieved more significant results.
其他文献
轧钢厂常使用转盘来实现轧材的旋转和升降运动,其运动是依靠安装在转盘旋转主轴上的圆柱形辊子(直径φ155mm、长70mm)沿着辊板的螺旋面滚动而实现的。辊板形状如图1所示,圆
焊接技术是许多现代工业部门的基本生产手段,如汽车、锅炉、家用电器、飞机制造等工业部门。可以大致的说,没有现代焊接技术的迅速发展,就不会有现代工业和科学技术的发展。
本文结合金塘大桥项目部的情况,从成本管理的角度阐述了该项目成本管理方面的特点。
Based on the project of Jintang Bridge Project Department, this article elaborate
本文介绍了用砂带磨削装置在10米龙门刨床上解决了4000吨平板硫化机、6450吨刨花板热压机产品上的大型加热板加工的关键。从而为今后的大型平面加工提供了一项新的工艺方法。
根据“压力容器安全监察规程”(以下简称“规程”)第43条l、3规定,容器出厂前应按要求制作焊接试板(以下简称试板),并作机械性能试验(σ_b、α_k、冷弯等)。试板机械性能试
30多年前由赛米控公司发明的世界上第一颗绝缘功率模块SEMIPACK现已发展到了第6代。对于电流从20A到118A的应用来说,SEMIPACK 1沿用了前几代产品的基本设计,但是电流输出能力
在系统分析京哈高速公路北运河大桥病害及成因的基础上,针对桥梁出现的裂缝、混凝土缺陷和支座损伤,采用裂缝灌浆封闭裂缝、混凝土缺陷修补和替换支座等技术措施进行了耐久性
BACKGROUND: 3, 4-methylenedioxymethamphetamine (MDMA, also known as “ecstasy”) hasbeen shown to exhibit neurotoxic effects on the hippocampus. However, expos
素混凝土产生冻胀破坏的因素是气温、土质、水分;预防方法是:加塑料膜、采用“U”型渠槽,采用浆砌或干砌重力式、复合式档土墙,换填非冻胀性土、设柔缝、使用技术和质量过硬
正弦规通常只用于测量斜度,但配合使用一只圆柱,通过一定计算,就可以在许多情况下用来测定空间尺寸,具有用途广泛和精确、简便的优点。下面先推导出基本方程,再举若干实例。