【摘 要】
：
La0.8Sr0.2MnO3 samples with rhombohedral, orthohombic and monoclinic structures were prepared by solid state reaction, sol-gel and co-precipitation methods, respectively. Lattice parameters, grain size, morphology, infrared absorption and emissivity of sa
【机 构】
：
AnHui Province Key Laboratory of Metallurgy Engineering & Resources Recycling, Anhui University of T
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
La0.8Sr0.2MnO3 samples with rhombohedral, orthohombic and monoclinic structures were prepared by solid state reaction, sol-gel and co-precipitation methods, respectively. Lattice parameters, grain size, morphology, infrared absorption and emissivity of samples were investigated. The results indicated that the average crystallite size calculated from XRD result and particle size of orthohombic sample were smaller than those of the other two samples, and honeycomb shape grains were observed in orthohombic sample. Due to lower crystal symmetry, Mn-O stretching vibration peaks of the three samples shifted to higher infrared wavenumber. According to the theory of wave optics and Kirchhoff law, bigger rhombohedral sample showed higher emissivity than monoclinic one. However, due to the honeycomb structure of orthohombic sample, repeated reflection and scattering led to the increase of absorption, and orthohombic sample exhibited the highest emissivity.
其他文献
Al foam sandwich panel (AFS) with metallic bonding was fabricated by foaming a hot-pressed three-layer composite with two steel facesheets and a melt route precursor as core. The melt route precursor was fabricated by dispersing undecomposed blowing agent
To improve the weak corrosion resistance of silicon steel to acid solution and alkaline solution with high temperature, a stable hierarchical micro/nanostructure superhydrophobic surface with myriad irregular micro-scale hump and sheet-like nanostructure
Optimizing highly porous fibrous ceramics, like bird\'s nest structure, were obtained by vacuum impregnation method with mullite fibers and alumina sol as raw material. The influences of impregnation cycles on the property of the sample, such as porosit
A novel method to prepare an electrocatalyst with a new structure and high catalytic performance was reported. Two-dimensional (2D) PtRu nanoclusters have been successfully deposited on graphene oxide and carbon black supports. Compared with the commercia
Five types of KNO3-NH4VO3-rare earth metal nitrate (K-V-rare earth metal) catalysts supported on α-porous alumina ceramic substrates were prepared by a coating method. All the catalysts were characterized by X-ray diffraction and thermogravimetry/differen
In order to improve the efficiency of β-CD, the inclusion complex of β-CD and resorcinol bisdiphenylphosphate (RDP) (β-CD@RDP) was prepared, which β-CD was as the host component and RDP was as the guest. The structure and thermal stability property of β-C
The p-type Ge doped Fe0.4Co3.6Sb12-xGex skutterudites with multi-scaled impurity dots (500 nm-2 mm) were successfully prepared by using melt-quenching (MQ) and subsequent spark plasma sintering (SPS) technique. Compared with traditional method, the new te
The CaCu3Ti4O12 (CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process (synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investiga
The dimpling defects caused by conventional hemispherical punch in doubly curved sheet metal reconfigurable die forming process were considered. The rotatable cubic punch (RCP) was developed to suppress the dimpling defects more effectively and convenient