【摘 要】
：
The equations of hydrogen solubility in pure magnesium and its alloy were deduced based on thermodynamic analysis: for pure magnesium, lgc(H)=0.5lg p(H2)-1 332/
【机 构】
：
State Key Laboratory of Material Processing and Die & Mould Technology
论文部分内容阅读
The equations of hydrogen solubility in pure magnesium and its alloy were deduced based on thermodynamic analysis: for pure magnesium, lgc(H)=0.5lg p(H2)-1 332/T+0.568; for AZ91 alloy, lgc(H)=0.5lg p(H2)-1 332/T+0.483. Based on the above equations, a rapid and reliable measurement system for hydrogen content in magnesium melt was set up with CPU controller and electric circuit. With this instrument, measurement experiments were carried out to determine hydrogen content in AZ91 melt. The results show that the actual hydrogen level of AZ91 melt under gas protection varies from 0.06 mL/g to 0.14 mL/g at the temperature range from 650 ℃ to 750 ℃, and hydrogen content lineally increases with the increase of temperature.
其他文献
The carbon nanotube (CNT) growth of iron oxide-deposited trench-patterns and the locally-ordered CNT arrays on silicon substrate were achieved by simple thermal
Electrochemical methods were applied to investigate the corrosion behaviour of LY12CZ under applied stress in 3% sodium chloride aqueous solution. The experimen
A new metastable beta titanium alloy of Ti-Al-Mo-V-Cr-Fe-Zr-Sn system was designed and named Ti-B20. In order to investigate the aging properties and microstruc
Mg-6Al-4RE-0.4Mn (mass fraction, %, RE=Ce rich mischmetal) alloy was prepared by steel mould casting technique. Solid solution and artificial aging (T6) were ca
Y-shaped structure was synthesized by ethanol catalytic combustion(ECC) technique on the copper plate substrate,without directly seeding catalyst into the flame
Mg-(5-22)(mass fraction, %)Li alloys with Zn addition were produced and studied. The density of studied alloys is 1.19- 1.62 g/cm3. It is found that the alloy h
InAs quantum dots (QDs) grown on InxGa1-xAs/InP matrix by low pressure metal organic vapor phase epitaxy (LP-MOVPE) in nitrogen ambient were studied. Formation
Single crystals of Ca3NbGa3Si2O14 (CNGS) with ordered Ca3Ga2Ge4O14 (CGG) structure were successfully grown from stoichiometric melts by conventional Czochralski
The acid treatment process,testing methods,microstrcture of sepiolite mineral materials and their adsorbing properties to dodecanol were studied respectively. T
The semi-solid compression deformation behaviour of Y112 die casting aluminum alloy with nondendritic structure obtained under the semi-solid isothermal treatme