The synthesis procedures and physical properties of the ambient dried hydrophobic silica aerogels by using different contents of ethanol(EtOH)/trimethylchlorosilane(TMCS)/n-Hexane as surface modification agent were investigated.One-step solvent exchange a
【机 构】
：
Institute of Building Materials, School of Civil and Hydraulic Engineering, Dalian University of Tec
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The synthesis procedures and physical properties of the ambient dried hydrophobic silica aerogels by using different contents of ethanol(EtOH)/trimethylchlorosilane(TMCS)/n-Hexane as surface modification agent were investigated.One-step solvent exchange and surface modification were simultaneously progressed by immersing silica hydrogels in EtOH/TMCS/n-Hexane solution.It is found that microstructures as well as properties of silica aerogels like porosity,specific density and specific surface area are affected by the contents of surface modification agent in the sol from the re-sults of SEM,TEM morphology,FT-IR chemical structure,BET surface area and BJH pore size analyses.The volume of TMCS is of 10%and 20%of hydrogels,and the final product is hydrophilic xerogels.When TMCS\'s percent(v/v)is elevated to 75%-100%,hydrophobic silica aerogels with good performance are synthesized,the porosities of aerogels are in the range of 93.5%-95.8%and the av-erage pore size diameter is less than 20 nm.
其他文献
Three dimensional(3D)printing technology was utilized to fabricate a new type of drug implant with complicated architectures,employing levofloxacin(LVFX)and rifampicine(RFP) as model drugs.The prepared drug implant prototype consists of a double-layer str
A solution method was developed for fabricating ZnO nanostructures using(NH_4)_2CO_3 as starting material. SEM analysis shows that ZnO nanostructures exhibit nanorod, branchand flower-like morphologies. The crystal phase of as-synthesized products was cha
A novel process for separation of red(Y_2O_3:Eu~(3+)),blue(BaMgAl_(10)O_(17):Eu~(2+))and green(CeMgAl_(10)O_(17):Tb~3)rare earth fluorescent powders was proposed.At first,the blue powder can be extracted selectively from an aqueous solution using a chelat
High performance cement based composite materials was prepared by adding epoxy emulsion.The epoxy emulsion was synthesized with epoxy phosphoric acid ester and poly-glycol in laboratory.This epoxy emulsion has advantages over other emulsion,such as dehydr
The durability of the cement was mainly studied.Under 1.0 MPa of hydraulic pressure for 8 hours,water could penetrate completely through the sample made by portland cement,but could not penetrate through that by alite-barium sulphoaluminate cement.Under t
Trace elements were determined in high purity gold by high resolution inductively coupled plasma mass spectrometry(HR-ICP-MS).Sample were decomposed by aqua regia.To overcome some potentially problematic spectral interference,measurements were acquired in