【摘 要】
：
Industrial big data was usually multi-source,heterogeneous,and deeply intertwined.It had a wide range of data sources,high data dimensions,and strong data corre
【机 构】
：
School of Computer Technology,Xi’an University of Posts and Telecommunications,Xi’an 710121,China;Sh
论文部分内容阅读
Industrial big data was usually multi-source,heterogeneous,and deeply intertwined.It had a wide range of data sources,high data dimensions,and strong data correlation.In order to effectively analyze and process streaming industrial big data generated by edge computing,it was very important to provide an effective real-time incremental data method.However,in the process of incremental processing,industrial big data incremental computing faced the challenges of dimensional disaster,repeated calculations,and the explosion of intermediate results.Therefore,in order to solve the above problems effectively,a QR-based tensor-train(TT)decomposition(TTD)method and a QR-based incremental TTD(QRITTD)method were proposed.This algorithm combined the incremental QR-based decomposition algorithm with an approximate singular value decomposition(SVD)algorithm and had good scalability.In addition,the computational complexity,space complexity,and approximation error analysis were analyzed in detail.The effectiveness of the three algorithms of QRITTD,non-incremental TTD(NITTD),and TT rank-1(TTrl)SVD(TTrl SVD)were verified by comparison.Experimental results show that the SVD QRITTD method has better performance under the premise of ensuring the same tensor size.
其他文献
With the expansion of wind speed data sets,decreasing model training time is of great significance to the time cost of wind speed prediction.And imperfection of
随着烟草行业的发展和国家安全生产要求的提高,烟草加工中粉尘爆炸隐患是烟草生产的潜在风险,如何消除隐患,避免危害发生,是当前烟草企业需要解决的问题。该文以滕州卷烟厂为例,介绍了一种以多通路数据传感器为数采基础,以PLC编程为逻辑控制单元,结合OPC数采,Web前端展示以及GSM通信技术的烟草企业粉尘防爆预警系统。该系统可以实时监控与粉尘爆炸相关的各类隐患指标,自动消除隐患,有效降低隐患发生概率,为烟草企业安全生产提供保障。
综述几种铜及铜合金表面处理技术的进展,包括离子液体镀技术、等离子喷涂技术、激光熔覆技术、激光合金化、激光表面淬火与重熔技术。以铜及铜合金为表面处理对象,通过表面处理补强铜材料耐蚀、耐磨等性能,拓宽其应用范围。围绕铜及铜合金基体因高导热、高反射率等特性带来的表面处理难题,对铜及铜合金典型表面处理技术的特点与优劣势进行对比与分析,展望这些技术在铜及铜合金表面处理方向上的趋势与潜力。
针对典型高速列车车体用6N01铝合金,对十字角接接头的显微组织和疲劳性能进行研究。结果表明:十字角接接头的焊缝组织为等轴状铸态组织;在热影响区,与淬火区晶粒尺寸相比,过时效区晶粒尺寸增大,同时析出大量Mg2Si相。显微硬度试验结果表明,十字角接接头的焊缝显微硬度最低,平均值为94.2 HV;热影响区的显微硬度平均值为111.6 HV,但在距离热影响区中心0.25 mm左右的区域,显微硬度下降至108.5 HV,形成软化区。室温环境下,获得应力比为0.5和-1的疲劳S-N曲线,与母材相比,十字角接接头的室温
To improve the anti-noise ability of fuzzy local information C-means clustering,a robust entropy-like distance driven fuzzy clustering with local information is
采用上引连铸-连续挤压技术制备Cu-0.88Cr-0.14Zr(质量分数)合金,并对挤压后的棒材进行不同制度的时效处理。利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、电子背散射技术(EBSD)等分析测试手段研究合金经不同工艺/制度处理后的组织与性能的变化。结果表明:上引连铸Cu-Cr-Zr合金棒坯在连续挤压过程中发生了剧烈的剪切变形和动态时效,晶粒明显细化,析出尺寸为15~20 nm的Cr相,与铸态相比,挤压态合金的导电率与硬度分别增加了28.6%IACS、49.6 HV。确定了挤压态合金杆材经
针对固溶态Mg-11Gd-4Y-2Zn-0.4Zr合金,利用金相显微镜(OM)、扫描电子显微镜(SEM)和电子背散射衍射(EBSD)技术结合剪应力等效施密特因子计算,系统研究该合金在350~450℃热扭转过程中组织演化规律及变形机理,为该合金剪切变形工艺的开发提供理论支撑。结果表明:扭转变形后,该合金原始等轴晶粒沿着剪切方向被拉长,同时,形成具有剪切特征的变形织构。350℃变形时,该合金变形机制以基面<a>滑移为主,部分晶粒发生拉伸孪晶,孪晶变体的选择满足施密特定律,且当基面<a>
采用疲劳强度及裂纹扩展测试、扫描电镜和电子背散射衍射等方法研究难溶结晶相分布特征对7020铝合金型材疲劳行为的影响。结果表明:合金中直径小于2μm的难溶结晶相占比较大,且数量较多;当直径大于4μm的难溶结晶相较少时,疲劳强度可达113.3 MPa,比含较多大尺寸难溶结晶相的合金疲劳强度高16.4%。当应力强度因子ΔK=10 MPa·m1/2时,含较多大尺寸难溶结晶相比含密集且细小的合金裂纹扩展速率快21.0%。直径在3~17μm的粗大难溶结晶相在疲劳循环中因自身开裂或与基体界面脱粘而易形成裂纹源,其中直径
稀土由于具有较强的吸附性,在电沉积过程中可以通过提高形核率、阻碍晶粒长大的方式来改善镀层组织,因此会对材料表面改性产生独特优势。稀土掺杂于合金镀层可以使晶粒团簇分布更加均匀,缓蚀晶界,保持晶粒的高度择优取向,增强镀层与基体的结合度,提高镀层的硬度、结合强度、抗氧化性及耐腐蚀性能。本文系统综述了稀土作为镀液添加剂和改善镀层性能的国内外研究现状,以及稀土在不同电沉积体系中的作用机理,提出了稀土在改善材料表面性能方面存在的问题及最有潜力的发展方向。
通过电弧侵蚀模拟实验、三维轮廓仪(3DOP)和扫描电镜(SEM)等,研究操作次数对Ag/ZnO电触头电弧侵蚀行为的影响。结果表明:不同操作次数下,Ag/ZnO电触头电弧能量概率分布与电弧时间概率分布相似,电弧能量平均值与电弧时间平均值变化趋势一致。当操作次数为10000次时,Ag/ZnO电触头的电弧能量、电弧时间、温度变化、质量变化均最大,而电阻率变化最小。随着操作次数的增加,Ag/ZnO电触头表面形貌变化越来越大;相同操作次数下,阳极电触头表面形貌变化比阴极大。在电弧作用下,Ag/ZnO电触头主要发生喷