对生物医用锆合金表面进行热氧化改性处理,研究了氧化温度、氧化时间和冷却方式对改性层硬度、结合强度及膜厚的影响,并采用正交优化法进行分析。最终确定出一套综合性能较优
论文部分内容阅读
对生物医用锆合金表面进行热氧化改性处理,研究了氧化温度、氧化时间和冷却方式对改性层硬度、结合强度及膜厚的影响,并采用正交优化法进行分析。最终确定出一套综合性能较优的氧化工艺,即经700℃加热、8 h氧化保温及随炉冷却处理,所获得的氧化锆膜层硬度达到1258 HV,与基体硬度199 HV相比,提高了5倍多,同时得到较好的结合度。
The effects of oxidation temperature, oxidation time and cooling mode on the hardness, bonding strength and film thickness of the modified layer were studied and the orthogonal optimization method was used to analyze the surface of the biomedical zirconium alloy. Finally, a set of oxidation process with better comprehensive performance was finally determined, that is, the hardness of the obtained zirconium oxide film reached 1258 HV after being heated at 700 ° C for 8 h and then cooled in the furnace, and the hardness was increased as compared with the substrate hardness of 199 HV More than 5 times, at the same time get a better degree of integration.
其他文献
目的:探讨心率变异性(HRV)和QT间期离散度(QTd)对冠心病患者行经皮冠状动脉介入术(PCI)后发生心血管事件的预测价值.方法:对我院80例行PCI的冠心病患者进行手术前后的动态心
边坡失稳破坏是岩土工程中常遇到的工程问题之一,因此,在工程设计中,常根据需要进行边坡稳定性分析计算。常用的边坡稳定分析方法是安全系数法,它是经过长期工程实践证明的一
当前高等职业卫生学校医学类教师的继续医学教育注重专业课理论知识的培训,忽略了技能培训及人文素养和职业道德教育.随着教育模式的转变,新型的做中学教育模式,对医学类人才
目的探讨蜈蚣提取液对裸鼠移植肝癌的治疗作用及机制。方法建立裸鼠Bel-7404人异位肝癌移植模型,以蜈蚣提取液灌胃31d后,用免疫组化法对肿瘤组织标本进行X染色体连锁凋亡抑制
Noncompaction of the ventricular myocardium is a rare congenital heart disease and its main clinical manifestations are heart failure,thrombosis and arrhythmias
小学语文课程的内容是丰富多彩的,而如何将这丰富的学科知识传授给学生,使学生在习得知识的同时发展能力,实现知识与情感、技能与态度的同步发展,是现今语文教师要关注的主要
目的:通过对踝臂脉搏波速(baPWV)的检测分析,探究baPWV对冠心病的预测及临床筛查的价值.方法:从1 460例接受选择性冠状动脉(冠脉)造影或冠脉CTA检查的患者中,筛选出冠心病患
通过950℃下Cr-Y2O3扩散共渗5 h的方法在超级13Cr表面制备了Cr-Y共渗层,采用SEM、EDS和XRD分析了共渗层的结构及相组成,并对超级13Cr基体及共渗层的常温耐磨性进行了研究。结
国家能源核电站仪表研发与试验中心全面建成了具有独立第三方地位的核电仪控产品“一站式”试验验证平台,全部试验能力获得了中国合格评定国家认可委员会的认可,已经为核电行
目的:探讨肥胖老鼠体内心脏、动脉与脂肪组织中骨形态发生蛋白4(BMP4)的表达及其与炎症程度的相关性。方法:将ob/ob小鼠分为实验组与干扰组,以C57BL/6小鼠为对照组。每组各8